Effect of an atelocollagen-loaded hyaluronic acid-based porous scaffold on healing in a rabbit model of chronic rotator cuff tear.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Rhee Sung-Min, Im Pilseon, Im Jihye, Kim Myung Seo, Ko Jae Hyeock, Oh Joo Han, Rhee Yong Girl, Kim Jaeyun
Аннотация
BACKGROUND: High re-tear rates following rotator cuff repair are largely due to poor tendon-to-bone healing and fibrotic tissue formation. Hyaluronic acid (HA) and atelocollagen have demonstrated potential for improving tendon healing, but their injectable forms suffer from rapid diffusion and limited retention at the repair site. We hypothesized that an atelocollagen-loaded HA porous scaffold would demonstrate excellent structural, mechanical, and biological properties in vitro and promote superior tendon healing in a rabbit model of chronic rotator cuff tear.
STUDY DESIGN: Controlled laboratory study.
METHODS: The porous HA scaffold was synthesized via cryogelation and reinforced with VICRYL mesh. In vitro characterization included macroporosity (∼100-200 μm), swelling behavior, compressive strength under cyclic loading, and pore interconnectivity. Atelocollagen loading and retention were assessed through injection and agitation tests, while biocompatibility was evaluated using C2C12 myoblasts in a transwell culture system. For in vivo analysis, 32 rabbits underwent bilateral chronic supraspinatus tendon detachment and delayed repair, and were randomized into 4 groups: (A) saline injection, (B) HA scaffold only, (C) atelocollagen injection, and (D) atelocollagen-loaded HA scaffold. At 12 weeks postrepair, histological scoring, gene expression, and biomechanical testing were performed.
RESULTS: The porous scaffold exhibited high mechanical resilience, stable atelocollagen retention within macropores, and excellent biocompatibility with no cytotoxic effects. VICRYL reinforcement enabled firm suture retention without tearing, confirming surgical applicability. In vivo, Group D demonstrated significantly greater collagen fiber density (P = .041) and higher tendon stiffness (42.2 ± 7.5 N/mm; P = .005) compared to other groups. Load-to-failure values were highest in Group D but not statistically significant. No significant differences were observed in gene expression among groups at 12 weeks.
CONCLUSION: The atelocollagen-loaded HA porous scaffold offers a structurally stable, biocompatible platform capable of sustained therapeutic delivery. It significantly enhanced collagen organization and mechanical strength in a chronic rotator cuff tear model, supporting its potential as an effective adjunct to tendon repair.
STUDY DESIGN: Controlled laboratory study.
METHODS: The porous HA scaffold was synthesized via cryogelation and reinforced with VICRYL mesh. In vitro characterization included macroporosity (∼100-200 μm), swelling behavior, compressive strength under cyclic loading, and pore interconnectivity. Atelocollagen loading and retention were assessed through injection and agitation tests, while biocompatibility was evaluated using C2C12 myoblasts in a transwell culture system. For in vivo analysis, 32 rabbits underwent bilateral chronic supraspinatus tendon detachment and delayed repair, and were randomized into 4 groups: (A) saline injection, (B) HA scaffold only, (C) atelocollagen injection, and (D) atelocollagen-loaded HA scaffold. At 12 weeks postrepair, histological scoring, gene expression, and biomechanical testing were performed.
RESULTS: The porous scaffold exhibited high mechanical resilience, stable atelocollagen retention within macropores, and excellent biocompatibility with no cytotoxic effects. VICRYL reinforcement enabled firm suture retention without tearing, confirming surgical applicability. In vivo, Group D demonstrated significantly greater collagen fiber density (P = .041) and higher tendon stiffness (42.2 ± 7.5 N/mm; P = .005) compared to other groups. Load-to-failure values were highest in Group D but not statistically significant. No significant differences were observed in gene expression among groups at 12 weeks.
CONCLUSION: The atelocollagen-loaded HA porous scaffold offers a structurally stable, biocompatible platform capable of sustained therapeutic delivery. It significantly enhanced collagen organization and mechanical strength in a chronic rotator cuff tear model, supporting its potential as an effective adjunct to tendon repair.