Biological Evaluation of Two Magnesium Alloys from Mg-Zn-Mn-Ca and Mg-Nd-Y-Zr-Zn Systems for Bone Repair and Regeneration.

Background and

Objectives

Magnesium-based biomaterials are increasingly investigated due to their biodegradability, bone-like elastic modulus, and potential osteogenic properties. However, alloy composition may influence degradation behavior and local tissue response. This study aimed to assess and compare the local biocompatibility, degradation characteristics, and bone regenerative response induced by Mg-Zn-Mn-Ca and Mg-Nd-Y-Zr-Zn magnesium alloy powders. Materials and

Methods

Two magnesium alloys were evaluated through physicochemical characterization, in vitro osteoblast cytocompatibility and antimicrobial assays, and in vivo testing in Sprague-Dawley rats. Standardized cylindrical defects were created in the medial femoral condyle and filled with either Mg-Nd-Y-Zr-Zn or Mg-Zn-Mn-Ca alloy powders, while untreated defects served as controls. Bone remodeling and defect healing were assessed by micro-computed tomography, allowing three-dimensional qualitative and quantitative evaluation of newly formed bone. Scanning electron microscopy was used to analyze surface morphology and degradation features, while histopathological examination assessed inflammation, osteogenesis, and tissue integration at the implant site.

Results

Both magnesium alloy powders showed antimicrobial potency and elicited no cytotoxic effects in vitro, while animal studies revealed progressive biodegradation over time, associated with new bone formation within and around the defect area. Micro-CT analysis demonstrated active bone remodeling in experimental groups, with differences in bone distribution and defect-filling patterns between Mg-Nd-Y-Zr-Zn and Mg-Zn-Mn-Ca implants. SEM revealed alloy-specific degradation morphologies. Histological evaluation showed a moderate early inflammatory response that decreased at later time points, together with ongoing osteogenesis and favorable tissue integration. No severe local adverse reactions or persistent inflammation were observed.

Conclusions

Both Mg-Nd-Y-Zr-Zn and Mg-Zn-Mn-Ca alloy powders were locally biocompatible and supported bone regeneration in a rat femoral condyle defect model. Differences in degradation behavior and tissue response emphasize the relevance of alloy composition in developing magnesium-based biomaterials for bone defect treatment.