Clinical orthopaedics and related research · 2013
Severe metal-induced osteolysis many years after unipolar hip endoprosthesis.
Клинический случайСтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Mann Matthew A, Tanzer Dylan, Tanzer Michael
Аннотация
BACKGROUND: Modularity of the femoral head-neck junction provides increased intraoperative flexibility to the surgeon. Complications of this modularity include damage to the trunnion, with subsequent bone and/or soft tissue loss from adverse reactions to metal debris.
CASE DESCRIPTION: We describe two cases of severe metal-induced osteolysis and soft tissue damage requiring revision 10 and 13 years following implantation of a unipolar endoprosthesis. Damage to the trunnion resulted in severe acetabular and trochanteric osteolysis and soft tissue loss requiring complex revision surgery.
LITERATURE REVIEW: Several reports have shown the trunnion, the head-neck interface, and the neck-stem couple as the causes of this early failure secondary to metal ion release from mechanical fretting corrosion or from crevice corrosion at these modular interfaces. These reports have been in association with a total hip prosthesis rather than a unipolar endoprosthesis. Revision of a unipolar endoprosthesis is most commonly attributable to stem loosening or acetabular erosion from the large femoral head articulating on the host acetabular cartilage and not owing to failure of the trunnion.
PURPOSES AND CLINICAL RELEVANCE: Trunnion damage resulting in a severe reaction to metal debris with acetabular osteolysis, erosion of the greater trochanter, and loss of the abductor mechanism can occur years after implantation of a cementless unipolar endoprosthesis. This raises questions regarding long-term safety of the modular interface of a contemporary cementless stem and a large-diameter unipolar head. We recommend long-term followup of patients with a unipolar endoprosthesis as early recognition and treatment are required to avoid a potentially complex revision.
CASE DESCRIPTION: We describe two cases of severe metal-induced osteolysis and soft tissue damage requiring revision 10 and 13 years following implantation of a unipolar endoprosthesis. Damage to the trunnion resulted in severe acetabular and trochanteric osteolysis and soft tissue loss requiring complex revision surgery.
LITERATURE REVIEW: Several reports have shown the trunnion, the head-neck interface, and the neck-stem couple as the causes of this early failure secondary to metal ion release from mechanical fretting corrosion or from crevice corrosion at these modular interfaces. These reports have been in association with a total hip prosthesis rather than a unipolar endoprosthesis. Revision of a unipolar endoprosthesis is most commonly attributable to stem loosening or acetabular erosion from the large femoral head articulating on the host acetabular cartilage and not owing to failure of the trunnion.
PURPOSES AND CLINICAL RELEVANCE: Trunnion damage resulting in a severe reaction to metal debris with acetabular osteolysis, erosion of the greater trochanter, and loss of the abductor mechanism can occur years after implantation of a cementless unipolar endoprosthesis. This raises questions regarding long-term safety of the modular interface of a contemporary cementless stem and a large-diameter unipolar head. We recommend long-term followup of patients with a unipolar endoprosthesis as early recognition and treatment are required to avoid a potentially complex revision.