Analysis of calcium deposits in calcific periarthritis.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Hamada J, Ono W, Tamai K, Saotome K, Hoshino T
Аннотация
OBJECTIVE: To determine if hydroxyapatite (HAP), octacalcuim phosphate (OCP), or tricalcium phosphate (TCP) can be found in the calcium deposits in calcific periarthritis.
METHODS: Thirty-six specimens from 34 patients who had acute inflammation and roentgenographically recognized calcification in soft tissue were analyzed. Twenty-three patients with calcific tendinitis in the shoulder and 11 with calcific periarthritis at other sites were included. We prepared 2 kinds of samples from each specimen; a dried sample (washed and dried calcific deposit), and a sample heated to 1,000 degrees C. All were analyzed by X-ray diffraction, Raman spectroscopy, infrared absorption spectroscopy, and X-ray fluorescence spectrometry for calcium and phosphorus molar ratio. Synthetic HAP was used as the control in each analysis.
RESULTS: The X-ray diffraction patterns of all dried samples were similar to those of HAP and carbonate apatite. We found no diffraction patterns of OCP or TCP. However, an OH- group at 3570cm(-1) was observed with Raman spectroscopy for samples heated to 1,000 degrees C and synthetic HAP, but not for the dried samples. Infrared absorption spectroscopy also confirmed an OH- group for samples heated to 1,000 degrees C and synthetic HAP, and confirmed that dried samples contained carbonate.
CONCLUSION: Calcium deposits are composed of carbonate apatite. HAP, OCP, and TCP were not identified in any deposits.
METHODS: Thirty-six specimens from 34 patients who had acute inflammation and roentgenographically recognized calcification in soft tissue were analyzed. Twenty-three patients with calcific tendinitis in the shoulder and 11 with calcific periarthritis at other sites were included. We prepared 2 kinds of samples from each specimen; a dried sample (washed and dried calcific deposit), and a sample heated to 1,000 degrees C. All were analyzed by X-ray diffraction, Raman spectroscopy, infrared absorption spectroscopy, and X-ray fluorescence spectrometry for calcium and phosphorus molar ratio. Synthetic HAP was used as the control in each analysis.
RESULTS: The X-ray diffraction patterns of all dried samples were similar to those of HAP and carbonate apatite. We found no diffraction patterns of OCP or TCP. However, an OH- group at 3570cm(-1) was observed with Raman spectroscopy for samples heated to 1,000 degrees C and synthetic HAP, but not for the dried samples. Infrared absorption spectroscopy also confirmed an OH- group for samples heated to 1,000 degrees C and synthetic HAP, and confirmed that dried samples contained carbonate.
CONCLUSION: Calcium deposits are composed of carbonate apatite. HAP, OCP, and TCP were not identified in any deposits.