Influence of crack length and anatomical location on the fracture toughness of annulus fibrosus.

Fracture toughness (Jc) of a soft biological tissue is an important mechanical property that characterizes its resistance to crack or tear extension. To date, no information is available on fracture toughness of annulus fibrosus (AF); therefore, its defect tolerance is not known. The present study modified a previously introduced method to determine Jc of ovine AF. Then, the effect of the notch length on the failure pattern and Jc was investigated. Also, the test samples of anterior and lateral regions were collected to determine the effect of the location on Jc. Results showed that for a notch length of less than 45% of total width, no crack extension occurred, but for a notch length above 45% of the width, crack propagation and ultimately the failure of the AF were observed. However, statistical analysis indicated no significant difference on Jc (p = 0.5) for the initial notch length of 50% and 70% of total width. The fracture toughness was significantly higher for the samples extracted from the lateral site than those from the anterior site (p < 0.05). Dissimilar failure patterns were observed for different initial notch lengths. Among the parameters studied, the defect tolerance of AF was dependent on the initial tear size.