Biodegradable Dual-Function Nanocomposite Hydrogels for Prevention of Bisphosphonate-Related Osteonecrosis of the Jaw.

This study presents the development of composite hydrogels, comprising a biodegradable polymer (carboxymethyl chitosan (CMCS or CM)) and a mixture of plasma-treated mesoporous silica nanoparticles (PMCM-41 or PM) and amine-functionalized mesoporous silica nanoparticles (NMCM-41 or NM), coloaded with a hydrophilic antibiotic (clindamycin hydrochloride (CDM or C)) and a poorly water-soluble compound (geranylgeraniol (GGOH or G)) for prevention of bisphosphonate-related osteonecrosis of the jaw (BRONJ). The CG-loaded hydrogel stabilities were better maintained when CDM-preloaded PMCM-41 and NMCM-41 were initially used and governed by weight ratios of CDM-loaded PMCM-41 to NMCM-41 and CDM quantity utilized. 5PM240C-1NM-CM demonstrated the best CDM-loaded hydrogel for GGOH postloading. The scanning electron microscopy (SEM) and X-ray microcomputer-tomography (μCT) images of 5PM240C-1NM-CM revealed a porous structure with homogeneously distributed nanoparticles. Two GGOH-loaded 5PM240C-1NM-CM hydrogels were generated after GGOH loadings. Their biphasic drug release profiles were fitted by Ritger-Peppas and Hixson-Crowell models. The copresence of GGOH could hinder CDM releases, while GGOH was released with a slower rate. The hydrogels prolonged the CDM and GGOH releases up to 9 days. They possessed antibacterial activities against Streptococcus sanguinis for up to 14 days and satisfactorily provided good cytoprotection against zoledronic acid for osteoclastic and osteoblastic progenitors, thus preserving a pool of viable progenitor cells that had the capacity to differentiate into mature osteoclasts and osteoblasts in vitro, suggesting their potential local application for prevention of BRONJ.