Experimental studies on bone induction using low-molecular-weight poly (DL-lactide-co-glycolide) as a carrier for recombinant human bone morphogenetic protein-2.

An appropriate carrier acting as a slow delivery vehicle for the BMPs is required for maximal clinical effectiveness of these bone-inductive proteins. The purpose of this study was to evaluate a low-molecular-weight PLGA copolymer as a synthetic, biodegradable carrier for rhBMP-2 implantation in vivo. Two, 10, or 50 microg of recombinant human BMP-2 were mixed with 10 mg of a poly (DL-lactide-co-glycolide) (PLGA) 50:50 copolymer and implanted into the calf muscles of Wistar rats. Soft X-ray analysis and histologic examination indicated that new bone formation occurred at all rhBMP-2-implanted sites within 3 weeks after implantation. Correlation of rhBMP-2 concentration with the amount of bone induction was confirmed by specific alkaline phosphatase activity and calcium content assay. In vitro analysis indicated that 78.5% of the PLGA copolymer was degraded to smaller molecular weight material after 14 days in PBS solution. It is suggested that rhBMP-2 was released in an active form at the implant site during the degradation of the copolymer, resulting in the induction of new bone formation. Thus this low-molecular-weight PLGA copolymer material represents a promising delivery vehicle for BMPs, and possibly other growth factors, around dental and orthopedic implants.