A Comparison Between the Growth of Naturally Occurring Three-Dimensional Cracks in Scalmalloy® and Pre-Corroded 7085-T7452 and Its Implications for Additively Manufactured Limited-Life Replacement Parts.

This paper is the first to reveal that the conventionally built aluminium alloy (AA) 7085-T7452 has mechanical properties, viz: a yield stress, ultimate strength, and an elongation to failure, that are similar to that of laser powder bed fusion (LPBF) built Scalmalloy®. Following this observation, the growth of cracks that nucleated from corrosion pits in AA7085-T7452 specimens that had been exposed to a 5 wt% NaCl salt fog environment at 35 °C according to ASTM B117-19 standard for fourteen days is then studied. The specimen geometries were chosen to be identical to those associated with a similar study on Boeing Space, Intelligence, and Weapon Systems (BSI&WS) LPBF built Scalmalloy®. This level of prior exposure led to pits in AA7085-T7452 that were approximately 0.5 mm deep with a surface width/diameter of up to approximately 1.5 mm. These pit sizes are broadly consistent with those leading to fatigue crack growth (FCG) in AA 7050-T7451 structural parts on the RAAF F/A-18 Classic Hornet fleet operating in a highly corrosive environment. Fatigue tests on these AA7085-T7452 specimens, under the same spectrum as used in the BSI&WS LPBF Scalmalloy® study, reveals that AA7085-T7452 and Scalmalloy® have similar crack growth histories. This, in turn, leads to the discovery that the growth of naturally occurring three-dimensional (3D) cracks in AA 7085-T7452 could be predicted using the crack growth equation developed for BSI&WS LPBF Scalmalloy®, albeit with allowance made for their different fracture toughness's. These findings suggest that Scalmalloy® may be suitable for printing parts for both current and future attritable aircraft.