Proportional Multiaxial Fatigue Behavior and Life Prediction of Laser Powder Bed Fusion Ti-6Al-4V with Critical Plane-Based Building Direction Variations.

Laser powder bed fusion (L-PBF) is an additive manufacturing technique that enables the fabrication of complex geometries through a layer-by-layer approach, overcoming limitations of conventional manufacturing. In this study, multiaxial low-cycle fatigue (MLCF) tests were conducted on L-PBF Ti-6Al-4V (Ti64) specimens built in four different orientations, selected based on critical plane orientations identified from rolled titanium. Under proportional strain-controlled loading, the cyclic softening behavior, mean stress response, and fracture mechanisms of the material were systematically investigated. The results show that L-PBF Ti64 exhibits a three-stage softening characteristic (continuous softening, stable, and rapid softening). Fatigue cracks primarily initiate from inner-surface lack-of-fusion defects. Crack propagation shows cleavage and quasi-cleavage characteristics with tearing ridges, river patterns, and multi-directional striations. Proposed KBMP life prediction model, incorporating λ and building direction parameters, was developed. The KBMP-λ model demonstrates optimal accuracy, providing a reliable tool for the design of L-PBF titanium components subjected to complex multiaxial fatigue loading with relative errors within 20%.