Shear Response of Ionizable Polymer Melts at the Crossover from Ionomers to Polyelectrolytes.

Nonlinear shear response of polymers is affected by inherent barriers for diffusive motion, including entanglements and topology. In ionizable polymers, ionic clusters further constrain the intrinsic dynamics of the polymers, significantly enhancing their viscosity. Here, using fully atomistic molecular dynamics simulations, the nonlinear shear response of ionizable polymers is presented, across the transition from the ionomer regime where distinctive clusters dominate the structure to the polyelectrolyte regime where clusters percolate, in polystyrene randomly sulfonated with fractions of SO3 - groups of f = 0.20 and 0.35, in pristine and tetrahydrofuran (THF) swollen polyelectrolyte melts. For f = 0.20, the ionic clusters first fracture into smaller clusters followed by splitting into individual ionic groups and eventually reform. At higher f, the clusters morph in shape but do not break under high shear. At very high shear rates, all of the chains stretch and recoil rapidly. As the shear rate is reduced, some chains stretch and recoil, while others remain largely unaffected by the shear. Macroscopically, for all systems, the shear viscosity displays initially an elastic response, followed by nonlinear shear stress overshoot and, eventually, a steady state. The evolution of viscosity with time and shear reflects that of the ionizable domains.