Long-term outcome of primary total hip arthroplasty with cementless bioactive glass ceramic bottom-coated implants and highly cross-linked polyethylene: A minimum 10-year analysis.

BACKGROUND

Cementless glass ceramics containing apatite and wollastonite (AW-GC) bottom-coated titanium hip implants were developed; early excellent clinical and radiographic results have been reported previously. This study aimed to investigate the long-term clinical and radiographic outcomes in detail, and the wear rate of HXLPE.

METHODS

We retrospectively evaluated 99 patients (117 hips) between November 2001 and December 2007. The survival rate was estimated using the Kaplan-Meier method. Hip joint function was evaluated using the Japanese Orthopaedic Association (JOA) score. The extent of radiographic signs was determined from the radiographs performed at the last follow-up. Polyethylene wear was measured using Martell's Hip Analysis Suite. We assessed the possible factors affecting the steady-state linear wear rate.

RESULTS

The mean follow-up period was 14.8 ± 2.1 (10-18.6) years. The mean JOA score improved to 88.7 ± 9.4 (59-100) at the final follow-up from 47.8 ± 12.5 (17-76) before surgery. The overall survival rate with the end point of all-cause revision and wear-related revision was 99% and 100% respectively. There was no osteolysis or loosening of either the acetabular or femoral component. All hips were classified as having bone ingrowth fixation. The mean steady-state wear rate was 0.008 ± 0.025 mm/year. We found no significant correlation between the wear rate and age, body weight, body mass index, cup inclination and femoral head size.

CONCLUSION

The combination of AW-GC bottom-coated implants and HXLPE showed excellent implant survival and wear resistance for 15 years.