A Study on the Low-Intensity Cracking Resistance of Drainage Asphalt Mixtures by Graphene/Rubber Powder Compound Modified Asphalt.

In order to investigate the influence of graphene/rubber powder compound modified asphalt on the low-temperature cracking resistance of drainage asphalt mixtures, graphene/rubber powder compound modified asphalt mixtures were prepared using graphene/rubber powder compound modified asphalt for drainage asphalt mixtures, and compared with SBS-modified asphalt and rubber powder-modified asphalt, and the low-temperature cracking resistance of graphene/rubber powder compound modification asphalt mixtures was investigated through the Marshall Stability Test, Semi-circular Bending Test (SCB), and Freeze-Thaw Split Test. Research was carried out. At the same time, a scanning electric microscope (SEM) was adopted to analyze the micro-mechanism of the graphene/rubber powder compound modified asphalt mixtures under the microscopic condition. The findings showed that graphene dispersed the aggregation of rubber powder effectively in the microscopic state and improved the stability of the composite modified asphalt. The addition of graphene improved the fracture energy of rubber powder composite modified asphalt by 15.68% under the condition of -15 °C to 0 °C, which effectively slowed down the decrease of fracture energy; at -15 °C and -10 °C, the largest stresses were improved by 7.50% and 26.71%, respectively, compared to the drainage asphalt mixtures prepared as rubber powder-modified asphalt and SBS-modified asphalt. After a freeze-thaw cycle, the maximum stress decrease of graphene/rubber powder compound modified asphalt was 21.51% and 10.37% at -15 °C and 0 °C, respectively. When compared to rubber powder-modified asphalt, graphene/rubber powder compound modified asphalt significantly improved the low-intensity cracking resistance of drainage asphalt mixtures at low temperatures, slowed down the decrease of the maximum stress, and its low-temperature cracking resistance was more stable.