Ultra-translucent zirconia crowns with antimicrobial glass coatings: fatigue life and antagonist wear analysis.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
da Silva Ana Carolina, Gouveia Silva Juliana de Freitas, Campos Tiago Moreira Bastos, Thim Gilmar Patrocínio, Jodha Kartikeya Singh, Marocho Susana Maria Salazar, Melo Marinho Renata Marques de, Griggs Jason Alan
Аннотация
OBJECTIVE: To evaluate the fatigue life of 5Y-PSZ crowns coated with antimicrobial glasses and the wear on the antagonist, comparing it to a commercial glaze.
METHODS: Forty-five crowns of 5Y-PSZ zirconia were divided into: commercial glaze (G); boron-doped soda-lime glass (BSL), and boron-doped soda-lime glass with silver (BSLAg). Step-stress accelerated life testing was conducted at 2 Hz with a stress ratio of 0.1 on a custom servo-hydraulic load frame. The characteristic lifetime and Weibull modulus were estimated using the ALTAPRO software. Energy-Dispersive Spectroscopy (EDS), surface roughness (SR, Sa, and Sz) for the coated crowns and the pistons, fractography, and piston wear analysis were conducted. Crown's SR and piston wear were analyzed by two-way ANOVA, and Tukey's method (α=0.05). Piston's SR was examined by Linear Mixed Model (LMM) (α=0.05).
RESULTS: EDS identified zirconium in the composition of the radiopaque structures on both experimental glass coating surfaces. Crowns coated by BSL showed the lowest Sz values after all the different fatigue profiles. After the fatigue test, the SR (Sa and Sz) of the piston for all groups was similarly higher than before. No significant difference could be detected between the groups after the fatigue lifetime analysis. Fractures originated at the glass surface for all groups. The pistons in contact with the G group crowns presented greater volume wear for the mild fatigue profile.
SIGNIFICANCE: 5Y-PSZ zirconia crowns coated by BSL and BSLAg maintained the fatigue performance and significantly reduced wear on the piston/antagonist compared to the commercial glaze group. These coatings show potential for clinical applications in ceramic restorations, particularly in environments prone to biofilm accumulation.
METHODS: Forty-five crowns of 5Y-PSZ zirconia were divided into: commercial glaze (G); boron-doped soda-lime glass (BSL), and boron-doped soda-lime glass with silver (BSLAg). Step-stress accelerated life testing was conducted at 2 Hz with a stress ratio of 0.1 on a custom servo-hydraulic load frame. The characteristic lifetime and Weibull modulus were estimated using the ALTAPRO software. Energy-Dispersive Spectroscopy (EDS), surface roughness (SR, Sa, and Sz) for the coated crowns and the pistons, fractography, and piston wear analysis were conducted. Crown's SR and piston wear were analyzed by two-way ANOVA, and Tukey's method (α=0.05). Piston's SR was examined by Linear Mixed Model (LMM) (α=0.05).
RESULTS: EDS identified zirconium in the composition of the radiopaque structures on both experimental glass coating surfaces. Crowns coated by BSL showed the lowest Sz values after all the different fatigue profiles. After the fatigue test, the SR (Sa and Sz) of the piston for all groups was similarly higher than before. No significant difference could be detected between the groups after the fatigue lifetime analysis. Fractures originated at the glass surface for all groups. The pistons in contact with the G group crowns presented greater volume wear for the mild fatigue profile.
SIGNIFICANCE: 5Y-PSZ zirconia crowns coated by BSL and BSLAg maintained the fatigue performance and significantly reduced wear on the piston/antagonist compared to the commercial glaze group. These coatings show potential for clinical applications in ceramic restorations, particularly in environments prone to biofilm accumulation.