Influence of Dentin Bonding and Interfacial Adhesion on the Flexural Properties of a 4 Mol% Yttria Partially Stabilized Zirconia.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
De Angelis Francesco, Buonvivere Matteo, Mancini Camilla, Rondoni Giuseppe Daniele, Vadini Mirco, D'Arcangelo Camillo
Аннотация
PURPOSE: 4 mol% yttria partially stabilized zirconia (4Y-PSZ) offers improved translucency compared to 3% tetragonal polycrystalline zirconia, but it lacks transformation toughening, which may affect its flexural strength. Because adhesive luting was shown to improve mechanical performance of all-ceramic materials, this research evaluated the influence of different cements on the three-point flexural strength of 4Y-PSZ bonded to bovine dentin.
MATERIALS AND METHODS: A total of 30 1-mm-thick dentin slices were obtained from bovine incisors, paired with 1-mm-thick 4Y-PSZ slices, and then divided into three groups (n = 10) based on the cement investigated: 10-MDP-free self-adhesive resin cement (SA), 10-MDP-based adhesive resin cement (MDP-A), and conventional glass-ionomer cement (GI). After luting, the obtained assemblies were cut to obtain 1-mm-wide bar-shaped specimens, which were subjected to the three-point bending test. Fracture loads and flexural strength were recorded, and the modes of failure were analyzed.
RESULTS: The highest fracture load and flexural strength were observed in the MDP-A group (76.5 N and 401.5 MPa), followed by the SA group (62.3 N and 326.8 MPa). The GI group exhibited the lowest values (45.6 N and 239.5 MPa). MDP-A group samples predominantly exhibited concurrent dentin and zirconia fractures without debonding, while in the SA and GI groups a frequent incidence of debonding at the interface was observed.
CONCLUSIONS: Adhesive cementation enhances the flexural strength of 4Y-PSZ bonded to bovine dentin, with the 10-MDP-based resin cement yielding the best performance. Effective adhesive techniques could improve the mechanical performance of 4Y-PSZ restorations, making them more reliable for clinical applications.
MATERIALS AND METHODS: A total of 30 1-mm-thick dentin slices were obtained from bovine incisors, paired with 1-mm-thick 4Y-PSZ slices, and then divided into three groups (n = 10) based on the cement investigated: 10-MDP-free self-adhesive resin cement (SA), 10-MDP-based adhesive resin cement (MDP-A), and conventional glass-ionomer cement (GI). After luting, the obtained assemblies were cut to obtain 1-mm-wide bar-shaped specimens, which were subjected to the three-point bending test. Fracture loads and flexural strength were recorded, and the modes of failure were analyzed.
RESULTS: The highest fracture load and flexural strength were observed in the MDP-A group (76.5 N and 401.5 MPa), followed by the SA group (62.3 N and 326.8 MPa). The GI group exhibited the lowest values (45.6 N and 239.5 MPa). MDP-A group samples predominantly exhibited concurrent dentin and zirconia fractures without debonding, while in the SA and GI groups a frequent incidence of debonding at the interface was observed.
CONCLUSIONS: Adhesive cementation enhances the flexural strength of 4Y-PSZ bonded to bovine dentin, with the 10-MDP-based resin cement yielding the best performance. Effective adhesive techniques could improve the mechanical performance of 4Y-PSZ restorations, making them more reliable for clinical applications.