In Vitro Evaluation of the Mechanical Properties of Posterior Adhesive Restorations Fabricated Using Three Different Techniques.

This study evaluates the optical properties and mechanical durability of adhesive restorations fabricated using different techniques for the treatment of single-tooth loss in the posterior region after an aging process. Sixty extracted human teeth (thirty molars and thirty premolars) were restored using three different fabrication methods: 3D-printed resin restorations, fiber mesh-reinforced direct composite restorations, and indirect composite restorations. Color stability was assessed using a spectrophotometer, and fracture resistance was measured using a universal testing machine. Finite element stress analysis (FEA) was conducted to validate mechanical test results under simulated intraoral conditions. The fiber-reinforced composite group exhibited the highest fracture resistance (1057.91 MPa), while 3D-printed restorations showed the lowest (p < 0.05). Regarding color stability, the fiber-reinforced group demonstrated the highest ΔE00 values (ΔE00 = 1.71), differing significantly from the other groups, while the 3D-printed and indirect composite restorations showed no significant difference. Mechanical test results were consistent with FEA findings. These results indicate that fiber reinforcement enhances mechanical durability in high-load-bearing areas, while 3D-printed restorations may not yet be suitable for posterior regions. However, their potential use in anterior restorations, where occlusal forces are lower, warrants further investigation to improve material properties.