Comparative analysis of Biodentine and Mineral Trioxide Aggregate repair High Plasticity in reinforcing roots with perforation: An in vitro study.

CONTEXT: Root perforation increases the fracture risk, and bioceramic materials can be used for repair. Evaluating the fracture resistance (FR) of these cements in teeth with simulated perforations is crucial for assessing their effectiveness.

AIM: The aim of the study was to evaluate the effect of Biodentine (Septodont, France) and Mineral Trioxide Aggregate High Plasticity (MTA Repair HP, Angelus, Brazil), on the FR of teeth with simulated root perforations.

DESIGN AND SETTINGS: An in vitro experimental design was conducted to compare and determine the most reliable repair and obturating material for root perforation.

MATERIALS AND

METHODS

Fifty extracted mandibular premolars were randomly assigned to one control group (n = 10) and four test groups (n = 10) based on the repair and backfilling materials used: Biodentine + gutta percha (GP) (Dentsply Maillefer, Germany) and AH Plus sealer (Dentsply, Germany), Biodentine + Biodentine, MTA HP + GP and sealer, and MTA HP + MTA HP. FR was assessed using a universal testing machine.

STATISTICAL ANALYSIS: The variance among the five groups was tested using Analysis of Variance and pairwise post hoc Tukey's test for intergroup comparisons. The level of statistical significance was set at P < 0.05.

RESULTS

The highest mean FR value was observed in the MTA HP + MTA HP group. ANOVA test revealed statistically significant differences between the groups (P < 0.05).

CONCLUSION

Bioceramic cements with a MOE similar to dentin enhance FR by forming a monoblock for uniform stress distribution. Perforation repair and backfilling with these cement reinforce the tooth.