Formation mechanism of radial and circular cracks promoted by delamination in drying silica colloidal deposits.

Cracks with radial and circular patterns are appealing in nature and industry. Although morphologies and propagation conditions of cracks are extensively studied, the formation mechanism of crack pattern by the interaction of channel fracture and interfacial delamination remains elusive. Here, we present the transition of radial to coexisting radial and circular crack patterns when the thickness of colloidal deposits on both hard and soft substrates exceeds a critical value, through the colloidal volume fraction dependence. In addition, a thickness-dependent phase diagram from radial crack to coexistence of radial and circular cracks was constructed with respect to the radius and the volume fractions of silica colloidal deposits. A phase-field fracture model is developed to elucidate how the formation of radial cracks is facilitated by simultaneous delamination. The warping-induced radial tensile stress at the bottom surface of the striped deposit is proportional to the thickness. It leads to subsequent nucleation and growth of circular cracks in thick deposits. This work provides insight into the formation mechanism of complex crack patterns in drying colloidal deposits and revolutionizes the design space of crack-based micro-nano structures.