The Journal of international medical research · 2024
Unstable Vancouver B1 periprosthetic femoral fracture fixation: A biomechanical comparison between a novel C-shaped memory alloy implant and cerclage wiring.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Oh Seog-Hyun, Suh Yu-Sung, Eghan-Acquah Emmanuel, Yurevich Kollerov Mikhail, Won Sung-Hun, Baek Min Jung, Lee Sung-Jae, Choi Sung-Woo
Аннотация
BACKGROUND: To compare the biomechanical stability of a novel, C-shaped nickel-titanium shape memory alloy (SMA) implant (C-clip) with traditional cerclage wiring in the fixation of a Vancouver B1 (VB1) periprosthetic femoral fracture (PFF).
METHODS: In total, 18 synthetic femoral fracture models were constructed to obtain unstable VB1 fracture with an oblique fracture line 8 cm below the lesser trochanter. For each model, the distal portion was repaired using a 10-hole locking plate and four distal bi-cortical screws. The proximal portion was repaired using either three, threaded cerclage wirings or three, novel C-shaped implants. Specimens underwent biomechanical testing using axial compression, torsional and four-point bending tests. Each test was performed on three specimens.
RESULTS: The C-clip was statistically significantly stronger (i.e., stiffer) than cerclage wiring in the three biomechanical tests. For axial compression, medians (ranges) were 39 (39-41) and 35 (35-35) N/mm, for the C-clip and cerclage wiring, respectively. For torsion, medians (ranges) were, 0.44 (0.44-0.45) and 0.30 (0.30-0.33) N/mm for the C-clip and cerclage wiring, respectively. For the four-point bending test, medians (ranges) were 39 (39-41) and 28 (28-31) N/mm; for the C-clip and cerclage wiring, respectively.
CONCLUSION: Results from this small study show that the novel, C-shaped SMA appears to be biomechanically superior to traditional cerclage wiring in terms of stiffness, axial compression, torsion and four-point bending, and may be a valuable alternative in the repair of VB1 PFF. Further research is necessary to support these results.
METHODS: In total, 18 synthetic femoral fracture models were constructed to obtain unstable VB1 fracture with an oblique fracture line 8 cm below the lesser trochanter. For each model, the distal portion was repaired using a 10-hole locking plate and four distal bi-cortical screws. The proximal portion was repaired using either three, threaded cerclage wirings or three, novel C-shaped implants. Specimens underwent biomechanical testing using axial compression, torsional and four-point bending tests. Each test was performed on three specimens.
RESULTS: The C-clip was statistically significantly stronger (i.e., stiffer) than cerclage wiring in the three biomechanical tests. For axial compression, medians (ranges) were 39 (39-41) and 35 (35-35) N/mm, for the C-clip and cerclage wiring, respectively. For torsion, medians (ranges) were, 0.44 (0.44-0.45) and 0.30 (0.30-0.33) N/mm for the C-clip and cerclage wiring, respectively. For the four-point bending test, medians (ranges) were 39 (39-41) and 28 (28-31) N/mm; for the C-clip and cerclage wiring, respectively.
CONCLUSION: Results from this small study show that the novel, C-shaped SMA appears to be biomechanically superior to traditional cerclage wiring in terms of stiffness, axial compression, torsion and four-point bending, and may be a valuable alternative in the repair of VB1 PFF. Further research is necessary to support these results.