Fracture Resistance and Push-Out Bond Strength of Three Post Types in the Restoration of Anterior Primary Teeth - A In Vitro study.
СтатьяСравнительное исследованиеНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Eltobgy Asmaa E, Elmalt Magda, Eldehna Alaa
Аннотация
CONTEXT: Restoration fractures and displacement are the two main causes of failure after the rehabilitation of severely worn primary anterior teeth.
AIMS: Compare the effect of three post types on the fracture and push-out bond strength.
METHODS AND MATERIALS: Sixty undamaged maxillary anterior primary teeth were allocated into three groups according to post type: (I) Tetric N Ceram composite post, (II) prefabricated glass fiber post, and (III) high viscous glass ionomer post. Each group was further subdivided into two sub-groups depending on the test used: fracture resistance test and push-out bond strength test. The all specimens were mounted in acrylic resin blocks and tested using a universal testing machine. The fracture and failure mode were determined by a stereomicroscope inspection of all the specimens. Data were analyzed by one-way analysis of variance (ANOVA) and the Bonferroni post hoc test ( P < 0.05).
RESULTS: There was a statistically significant difference between fracture resistance and push-out bond strength values for the experimental groups ( P < 0.05). The most significant fracture resistance value was in Group II and core/post fracture (restorable fracture) was the most obvious fracture in the three groups with the highest percentage in Group I. The most significant push-out bond strength value was in Group I and adhesive failure between dentin and luting cement/post was the most common type in the groups.
CONCLUSIONS: The fracture resistance and push-out bond strength were affected by the type of post ( P = 0.000). Prefabricated glass fiber posts showed the highest fracture resistance in this study. However, Tetric N Ceram composite posts had the most restorable fracture. Tetric N Ceram composite posts had the highest bond strength with adhesive failure mode.
AIMS: Compare the effect of three post types on the fracture and push-out bond strength.
METHODS AND MATERIALS: Sixty undamaged maxillary anterior primary teeth were allocated into three groups according to post type: (I) Tetric N Ceram composite post, (II) prefabricated glass fiber post, and (III) high viscous glass ionomer post. Each group was further subdivided into two sub-groups depending on the test used: fracture resistance test and push-out bond strength test. The all specimens were mounted in acrylic resin blocks and tested using a universal testing machine. The fracture and failure mode were determined by a stereomicroscope inspection of all the specimens. Data were analyzed by one-way analysis of variance (ANOVA) and the Bonferroni post hoc test ( P < 0.05).
RESULTS: There was a statistically significant difference between fracture resistance and push-out bond strength values for the experimental groups ( P < 0.05). The most significant fracture resistance value was in Group II and core/post fracture (restorable fracture) was the most obvious fracture in the three groups with the highest percentage in Group I. The most significant push-out bond strength value was in Group I and adhesive failure between dentin and luting cement/post was the most common type in the groups.
CONCLUSIONS: The fracture resistance and push-out bond strength were affected by the type of post ( P = 0.000). Prefabricated glass fiber posts showed the highest fracture resistance in this study. However, Tetric N Ceram composite posts had the most restorable fracture. Tetric N Ceram composite posts had the highest bond strength with adhesive failure mode.