Dielectric probing of low-temperature degradation resistance of commercial zirconia bio-ceramics.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Wang Bowen, Alazwari Rawan Saad, Ahmed Shafique, Hu Zimeng, Cattell Mike J, Yan Haixue
Аннотация
OBJECTIVES: To investigate the effect of the stability of oxygen vacancies on the low-temperature degradation (LTD) resistance of two kinds of commercial zirconia-based materials (3Y-TZP ceramics and Ce-TZP/Al2O3 composites) via the dielectric probing methods.
METHODS: The commercial 3Y-TZP ceramics and Ce-TZP/Al2O3 composites were prepared via conventional solid-state methods. Density, phase content, microstructure, strain, and biaxial flexural strength (BFS) of two materials were investigated using Archimedes method, XRD, SEM, strain-electric field (S-E) loops and ball-on-ring methods, respectively. The concentration of oxygen vacancies before and after LTD of two materials were evaluated using dielectric probing and XPS methods.
RESULTS: The XRD analysis revealed that compared to the 3Y-TZP ceramics, the Ce-TZP/Al2O3 composites showed better LTD resistance, without clear LTD. The greater LTD resistance for Ce-TZP/Al2O3 composites was associated with their stability of oxygen vacancies, by higher activation energy based on the dielectric measurements and XPS results. For the 3Y-TZP ceramics that underwent the tetragonal to the monoclinic phase transition during the LTD treatment, the concentration of their oxygen vacancies decreased after LTD. In addition, the Ce-TZP/Al2O3 composites exhibited higher flexural strength and potential fracture toughness based on the BFS testing and strain vs electric field measurement results, indicating a great potential for use in fixed restorative dental applications.
SIGNIFICANCE: This work suggested the stability of oxygen vacancies played a key role in the resistance to LTD. Optimizing the stability of the oxygen vacancies is key to the development of more reliable zirconia- based dental biomaterials with greater resistance to LTD.
METHODS: The commercial 3Y-TZP ceramics and Ce-TZP/Al2O3 composites were prepared via conventional solid-state methods. Density, phase content, microstructure, strain, and biaxial flexural strength (BFS) of two materials were investigated using Archimedes method, XRD, SEM, strain-electric field (S-E) loops and ball-on-ring methods, respectively. The concentration of oxygen vacancies before and after LTD of two materials were evaluated using dielectric probing and XPS methods.
RESULTS: The XRD analysis revealed that compared to the 3Y-TZP ceramics, the Ce-TZP/Al2O3 composites showed better LTD resistance, without clear LTD. The greater LTD resistance for Ce-TZP/Al2O3 composites was associated with their stability of oxygen vacancies, by higher activation energy based on the dielectric measurements and XPS results. For the 3Y-TZP ceramics that underwent the tetragonal to the monoclinic phase transition during the LTD treatment, the concentration of their oxygen vacancies decreased after LTD. In addition, the Ce-TZP/Al2O3 composites exhibited higher flexural strength and potential fracture toughness based on the BFS testing and strain vs electric field measurement results, indicating a great potential for use in fixed restorative dental applications.
SIGNIFICANCE: This work suggested the stability of oxygen vacancies played a key role in the resistance to LTD. Optimizing the stability of the oxygen vacancies is key to the development of more reliable zirconia- based dental biomaterials with greater resistance to LTD.