Water-Adaptive Microcapsules with a Brittle-Ductile-Brittle Transition Based on an O/W/O Emulsion for the Self-Healing of Cementitious Materials.

Cementitious materials inevitably develop cracks, posing a serious threat to the long-term security of infrastructure, especially in the complex underground environment of cementing engineering. Microcapsules are facing the problem of encapsulated structure damage during the mixing and breaking difficultly during self-healing when applied in cementitious materials, resulting in the decline of self-healing efficiency. Herein, the calcium alginate water-adaptive microcapsules (CaAlg-NS/E-51) were prepared via an O/W/O emulsion, and the water adaptability of the shell was applied to achieve a rapid brittle-ductile transition by absorbing water. The water adaptability of the microcapsule is conducive to resisting shear stress during stirring due to the decreased elastic modulus and the increased ductility of the shell when it absorbs water. Meanwhile, the water-bearing shell loses water and becomes brittle during dry curing, making it prone to fracture when self-healing. In the self-healing measurement, the self-healing efficiency of cementitious specimens with microcapsules absorbing water for 10 min improved by 234.9 and 60.0% at 1 and 7 days, respectively, compared with those containing dry microcapsules, owing to the water adaptability of the shell.