Computation of the fracture probability and lifetime of all ceramic anterior crowns under cyclic loading - An FEA study.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Liu Chao, Eser Atilim, Heintze Siegward, Rothbrust Frank, Broeckmann Christoph
Аннотация
OBJECTIVES: To predict the lifetime and fracture probability of anterior crowns made of a lithium disilicate glass-ceramic (IPS e.max CAD, LD, Ivoclar Vivadent, Liechtenstein) and a zirconia-containing lithium silicate glass-ceramic (Celtra Duo, ZLS, Dentsply Sirona, USA) under cycling loading.
METHODS: Three-point bending tests were conducted to measure the viscoelastic parameters. These parameters are used to compute the residual stresses of the anterior crown after crystallization. In the next analysis, the cyclic loading on the anterior crown was calculated. Based on this combined stress state (residual stress and stress state due to external cyclic loading), the life cycle and fracture probability of the anterior crown was calculated using the CARES/Life software. Finally, fatigue experiments were carried out to compare and validate the results of the computations.
RESULTS: Although a sound qualitative comparison of the lifetime of both materials can be done using this methodology, the calculated fracture probability of the anterior crown for both materials was very low in comparison with the fatigue test results using the fatigue parameters determined from the experiments. In order to achieve good correspondence with the experimental results, the SCG exponent n for both materials should be modified by a correlation factor of 0.38.
SIGNIFICANCE: Using this modified computational strategy, the results of the time-consuming fatigue tests for dental glass-ceramics can be closely predicted. This methodology can be integrated into the development process of new glass-ceramic materials in order to save time and costs.
METHODS: Three-point bending tests were conducted to measure the viscoelastic parameters. These parameters are used to compute the residual stresses of the anterior crown after crystallization. In the next analysis, the cyclic loading on the anterior crown was calculated. Based on this combined stress state (residual stress and stress state due to external cyclic loading), the life cycle and fracture probability of the anterior crown was calculated using the CARES/Life software. Finally, fatigue experiments were carried out to compare and validate the results of the computations.
RESULTS: Although a sound qualitative comparison of the lifetime of both materials can be done using this methodology, the calculated fracture probability of the anterior crown for both materials was very low in comparison with the fatigue test results using the fatigue parameters determined from the experiments. In order to achieve good correspondence with the experimental results, the SCG exponent n for both materials should be modified by a correlation factor of 0.38.
SIGNIFICANCE: Using this modified computational strategy, the results of the time-consuming fatigue tests for dental glass-ceramics can be closely predicted. This methodology can be integrated into the development process of new glass-ceramic materials in order to save time and costs.