Stress intensity factor of a cracked molar restored with different materials and designs: A 3D-FEA.
СтатьяПоддержка исследования: вне правительства СШАНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Jiang Jingang, Sun Jianpeng, Ma Hongyuan, Wang Jingchao, Huang Zhiyuan, Zhou Shan
Аннотация
OBJECTIVE: This work used 3D finite element analysis (FEA) to analyze and directly compare the stress intensity factor (SIF) and stress distribution at the crack tip of identical cracked tooth models restored with different materials and crown parameters.
METHODS: A 3D model of the cracked tooth was generated. Then, we applied 25 restorative models, including three parameters (shoulder height, width, and degree of polymerization), five restorative materials (GC, IPS, LU, ZC, VE), and two combinations of types of cement (RMGIC and GIC). An occlusal load of 800N was applied to the spherical part along the longitudinal axis. The stress distribution of the preparation and the SIF of the crack tip was analyzed.
RESULTS: The crack tip SIF was minimal for a shoulder height offset of 0.8 mm (P = 0.032), a shoulder width of 0.6 mm (P = 0.045), a crown material of ZC (P < 2e-16), and a cement material of RMGIC (P < 0.05), respectively. In contrast, the effect of different polymerization degrees on SIF was insignificant (P = 0.95).
CONCLUSION: Our results suggest that the selection of a larger modulus of elasticity (MOE) material for the crown, the preparation of a smaller shoulder width within a safe range, a reasonable increase in the crown length, and the selection of adhesive materials with high fracture toughness are favorable methods to prevent further crack extension.
METHODS: A 3D model of the cracked tooth was generated. Then, we applied 25 restorative models, including three parameters (shoulder height, width, and degree of polymerization), five restorative materials (GC, IPS, LU, ZC, VE), and two combinations of types of cement (RMGIC and GIC). An occlusal load of 800N was applied to the spherical part along the longitudinal axis. The stress distribution of the preparation and the SIF of the crack tip was analyzed.
RESULTS: The crack tip SIF was minimal for a shoulder height offset of 0.8 mm (P = 0.032), a shoulder width of 0.6 mm (P = 0.045), a crown material of ZC (P < 2e-16), and a cement material of RMGIC (P < 0.05), respectively. In contrast, the effect of different polymerization degrees on SIF was insignificant (P = 0.95).
CONCLUSION: Our results suggest that the selection of a larger modulus of elasticity (MOE) material for the crown, the preparation of a smaller shoulder width within a safe range, a reasonable increase in the crown length, and the selection of adhesive materials with high fracture toughness are favorable methods to prevent further crack extension.