An injectable, biodegradable calcium phosphate cement containing poly lactic-co-glycolic acid as a bone substitute in ex vivo human vertebral compression fracture and rabbit bone defect models.

UNLABELLED: Purpose/Aim of the study: To evaluate the biomechanical characteristics and biocompatibility of an injectable, biodegradable calcium phosphate cement (CPC) containing poly lactic-co-glycolic acid (PLGA).

MATERIALS AND

METHODS

A vertebral compression fracture model was established using 20 human cadaveric vertebrae (T11-L3) divided into CPC/PLGA composite versus PMMA groups for biomechanical testing. In addition, 35 New Zealand rabbits were used to evaluate biodegradability and osteoconductive properties of CPC/PLGA using a bone defect model. In vitro cytotoxicity was evaluated by culturing with L929 cells.

RESULTS

The CPC/PLGA composite effectively restored vertebral biomechanical properties. Compared with controls, the maximum load and compression strength of the CPC/PLGA group were lower, and stiffness was lower after kyphoplasty (all p <.05). Degradation was much slower in the control CPC compared with CPC/PLGA group. The bone tissue percentage in the CPC/PLGA group (44.9 ± 23.7%) was significantly higher compared with control CPC group (25.7 ± 10.9%) (p <.05). The viability of cells cultured on CPC/PLGA was greater than 70% compared with the blanks.

CONCLUSIONS

Our biodegradable CPC/PLGA composite showed good biomechanical properties, cytocompatibility, and osteoconductivity and may represent an ideal bone substitute for future applications.