Accelerated fatigue resistance and color stability of endodontically treated bleached maxillary incisors restored with and without a post.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Lemos Mori Ubaldini Adriana, Chmielewska Maja, Baesso Mauro Luciano, Haghparast Hadjir, Magne Pascal
Аннотация
PURPOSE: The present study aimed to assess fatigue resistance and color modifications of endodontically treated incisors (ETIs) submitted to internal bleaching and restored using three different techniques.
MATERIALS AND METHODS: Forty-five maxillary central incisors received endodontic treatment and were internally bleached. After the completion of bleaching, the ETIs were divided into three groups (n = 15) according to the different restoration procedures: 1) glass-ionomer cement base covered with composite resin (GI); 2) short fiber-reinforced composite resin base with composite resin (SF); 3) composite resin restoration over a fiberglass post (FP). Specimens were subjected to accelerated fatigue testing: frequency of 5 Hz, beginning with a load of 100 N for 5000 cycles and a 25-N load increase applied every 1700 cycles until a load of 1200 N was reached. Samples were loaded until fracture. The Kaplan-Meier survival analysis with the log-rank post hoc test were performed (α = 0.05). Tooth color was measured 4 weeks after the bleaching treatment and again after the final restoration procedure using a spectrophotometer and the Commission Internationale de l'Eclairage (CIE) L*a*b* system. L* values of the specimens were analyzed using the Shapiro-Wilk and paired sample t tests (α = 0.05).
RESULTS: All groups showed similar survival mean cycles until failure (P = 0.332) and presented a major number of nonrestorable failures. The GI group presented the lowest number of nonrepairable fractures (GI = 68%, SF = 79%, FP = 86%) and showed the most stable L* value (P = 0.987).
CONCLUSIONS: The fatigue survival of internally bleached ETIs was not affected by the restorative technique utilized. Retaining the glass-ionomer base and covering the surface with composite resin should provide optimal color stability.
MATERIALS AND METHODS: Forty-five maxillary central incisors received endodontic treatment and were internally bleached. After the completion of bleaching, the ETIs were divided into three groups (n = 15) according to the different restoration procedures: 1) glass-ionomer cement base covered with composite resin (GI); 2) short fiber-reinforced composite resin base with composite resin (SF); 3) composite resin restoration over a fiberglass post (FP). Specimens were subjected to accelerated fatigue testing: frequency of 5 Hz, beginning with a load of 100 N for 5000 cycles and a 25-N load increase applied every 1700 cycles until a load of 1200 N was reached. Samples were loaded until fracture. The Kaplan-Meier survival analysis with the log-rank post hoc test were performed (α = 0.05). Tooth color was measured 4 weeks after the bleaching treatment and again after the final restoration procedure using a spectrophotometer and the Commission Internationale de l'Eclairage (CIE) L*a*b* system. L* values of the specimens were analyzed using the Shapiro-Wilk and paired sample t tests (α = 0.05).
RESULTS: All groups showed similar survival mean cycles until failure (P = 0.332) and presented a major number of nonrestorable failures. The GI group presented the lowest number of nonrepairable fractures (GI = 68%, SF = 79%, FP = 86%) and showed the most stable L* value (P = 0.987).
CONCLUSIONS: The fatigue survival of internally bleached ETIs was not affected by the restorative technique utilized. Retaining the glass-ionomer base and covering the surface with composite resin should provide optimal color stability.