Strength of implant-supported lithium disilicate and polymer-infiltrated ceramic network restorations after thermomechanical aging.

AIM: To evaluate the fracture load and type of failure of two different monolithic restorative materials bonded to standardized titanium bases and fabricated by two different procedures regarding the bonding interface.

MATERIALS AND

METHODS

All screw-retained implant crown specimens (n = 40), subjected to fatigue by thermomechanical loading, differed in the restorative material (lithium disilicate [LDS] or polymer-infiltrated ceramic network [PICN], referred to as 'hybrid ceramic' [HYC]) and the interface type between the restorative material and the titanium base abutment (prefabricated ex-factory or produced during a CAM-milling procedure). This resulted in the following groups (n = 10/group): 1) LDS-M: lithium disilicate crown with a CAM-milled interface; 2) LDS-P: lithium disilicate crown with a prefabricated interface; 3) HYC-M: PICN crown with a CAM-milled interface; and 4) HYC-P: PICN crown with a prefabricated interface. Aged specimens underwent static fracture load testing. The load (N) at which the initial crack occurred was denoted as Finitial, and the maximal load (N) at which the restorations fractured as Fmax. All specimens were examined under a stereomicroscope to determine the failure mode.

RESULTS

The median Finitial values were 180 N for LDS-M, 343 N for LDS-P, 340 N for HYC-M, and 190 N for HYC-P. The median Fmax values were 1822 N for LDS-M, 2039 N for LDS-P, 1454 N for HYC-M, and 1581 N for HYC-P. The intergroup differences were significant for Finitial (KW: P = 0.0042) and for Fmax (KW: P = 0.0010). The failure types also showed differences between the restorative groups.

CONCLUSIONS

The choice of restorative material had a stronger influence on the fracture load than the abutment interface workflow. Lithium disilicate showed the highest load for initial crack appearance (Finitial) and for complete fracture of the restoration (Fmax).