Clinical implant dentistry and related research · 2022
Implant deformation and implant-abutment fracture resistance after standardized artificial aging: An in vitro study.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Zhai Zhihao, Nakano Tamaki, Chen Yuming, Watanabe Shota, Matsuoka Takashi, Ishigaki Shoichi
Аннотация
BACKGROUND AND PURPOSE: Zirconia abutments have been widely adopted in clinical implant practice. The unique mechanical properties of zirconia may significantly affect the long-term prognosis of implant treatments. The purpose of this study was to investigate the influence of abutment material on implant deformation and fracture resistance of internal conical connection implant-abutment complexes of two diameters after standardized artificial aging.
MATERIALS AND METHODS: Thirty original abutments (one-piece titanium, one-piece zirconia, zirconia with alloy base) with two diameters (regular, narrow) were connected to internal conical connection implants and subjected to a standardized artificial aging process consisting of thermal cycling and mechanical cyclic loading. Microcomputed tomography (μCT) scans of implant bodies were performed before and after aging. 3-dimensional images of implant bodies were generated from the μCT scans and aligned for before and after aging to calculate the volumetric deformation amount. Finally, fracture resistance was measured using a mechanical static loading test for the surviving aged and 30 brand-new specimens.
RESULTS: All specimens survived artificial aging. No significant difference in implant deformation was found in the regular groups (p = 0.095). In narrow groups, the one-piece zirconia group showed significantly less deformation (p < 0.0001). For fracture resistance, no significant decrease was observed after aging in any group (p > 0.05). One-piece zirconia abutments showed significantly lower strength than the other two materials for both diameters (p < 0.0001).
CONCLUSIONS: In the regular diameter system, abutment material had no significant influence on the tested mechanical property degradation after simulated long-term oral use. The mechanical performance of narrow diameter one-piece zirconia abutments differed from the other two materials. For optimal performance, one-piece zirconia abutments should be adopted only in anterior regions.
MATERIALS AND METHODS: Thirty original abutments (one-piece titanium, one-piece zirconia, zirconia with alloy base) with two diameters (regular, narrow) were connected to internal conical connection implants and subjected to a standardized artificial aging process consisting of thermal cycling and mechanical cyclic loading. Microcomputed tomography (μCT) scans of implant bodies were performed before and after aging. 3-dimensional images of implant bodies were generated from the μCT scans and aligned for before and after aging to calculate the volumetric deformation amount. Finally, fracture resistance was measured using a mechanical static loading test for the surviving aged and 30 brand-new specimens.
RESULTS: All specimens survived artificial aging. No significant difference in implant deformation was found in the regular groups (p = 0.095). In narrow groups, the one-piece zirconia group showed significantly less deformation (p < 0.0001). For fracture resistance, no significant decrease was observed after aging in any group (p > 0.05). One-piece zirconia abutments showed significantly lower strength than the other two materials for both diameters (p < 0.0001).
CONCLUSIONS: In the regular diameter system, abutment material had no significant influence on the tested mechanical property degradation after simulated long-term oral use. The mechanical performance of narrow diameter one-piece zirconia abutments differed from the other two materials. For optimal performance, one-piece zirconia abutments should be adopted only in anterior regions.