Probability of survival and failure mode of endodontically treated incisors without ferrule restored with CAD/CAM fiber-reinforced composite (FRC) post-cores.

PURPOSE: This study evaluated the probability of survival and failure mode of endodontically treated incisors without ferrule restored with CAD/CAM FRC post-cores.

METHODS

Root canals of bovine incisors were treated, leaving post preparations of ∼10 mm. Teeth were allocated into three groups: (i) cast metal post-core, (ii) FRC prefabricated post with a direct resin core build-up, and (iii) CAD/CAM FRC post-core. Posts and zirconia crowns were cemented using resin cement. Specimens were subjected to step-stress accelerated-life fatigue testing in water. Use level probability Weibull curves, probability of survival for a mission of 100,000 cycles at 25, 50, and 100 N, Weibull modulus, and characteristic strength were calculated and plotted. Failure mode was examined under a stereomicroscope.

RESULTS

Restored incisors demonstrated high probability of survival (93-100%) for missions estimated at 25 and 50 N, irrespective of post-core foundation. At 100 N, incisors restored with metal posts presented significantly higher probability of survival (99%) relative to CAD/CAM posts (79%), whereas FRC groups demonstrated no significant difference. Weibull analysis indicated no significant difference on the Weibull modulus (m = 3.38-5.92). Incisors reconstructed with metal post-cores (431 N) presented significantly higher characteristic strength relative to prefabricated (200 N) and CAD/CAM (202 N) FRC post-cores. While post fracture was the chief failure mode for prefabricated and CAD/CAM FRC post-cores, post and/or root fracture were the main event for metal post-cores.

CONCLUSION

Endodontically treated incisors without ferrule restored with CAD/CAM FRC post-cores presented promising probability of survival for loads compatible with anterior masticatory forces and favorable failure modes.