An in vivo preclinical study assessing biocompatibility of Pd-based bulk metallic glass.

BACKGROUND

The bulk metallic glass (BMG), Pd79Ag3.5P6Si9.5Ge2, has a high fracture toughness and has been found to accommodate post-yield stress, unlike most other BMG. Moreover, due to its greater noble gas composition it has a intrinsic corrosion resistance, ideal for dental and orthopedic implants.

OBJECTIVE

This present study aimed to evaluate the in vivo application of Pd79Ag3.5P6Si9.5Ge2 in a large translational sheep model to assess its efficacy to be utilized as an endosteal device.

METHODS

Twelve implants in the form of cylindrical rods (3 mm in diameter) were produced through rapid quenching. Each sheep (n = 12) received one osteotomy in the mandibular region using rotary instrumentation, which was filled with Pd79Ag3.5P6Si9.5Ge2. After 6- and 24-weeks the animals were euthanized, and samples collected en bloc to conduct histomorphometric analysis. The degree of osseointegration were assessed through bone-to-implant contact (BIC).

RESULTS

All samples revealed favorable BIC along with with fibrous connective tissue layers at both 6- and 24-weeks. Bone along with interfacial remodeling was observed in proximity with the metallic glass surface at 6 weeks with higher degrees of bone organization being observed at the later healing time, 24 weeks.

CONCLUSIONS

The synthesized BMG, given its unique combination of toughness and strength, revealed potential to serve as an alternative to commonly used Ti alloys.