Mechanical stability of angulated zirconia abutments supporting maxillary anterior single crowns on narrow-diameter implants.

OBJECTIVES

To investigate the fracture strength of angulated hybrid abutments supporting anterior single crowns on narrow-diameter implants (NDIs).

MATERIAL AND

METHODS

Zirconia abutment with angulations of labial inclination 0° (TZ0Z), 15° (TZ15Z), 30° (TZ30Z) and palatal inclination 15° (TZ - 15Z) was designed on 3.3-mm titanium-zirconium (Ti-Zr) NDIs. Titanium abutment connected with Ti-Zr implant (TZ0T) and 0° zirconia abutment connected with pure titanium (Ti) implant (T0Z) were control groups. Thirty-six un-restored abutments and 36 abutments restored with highly translucent zirconia (HTZ) crowns were tested. Failure loads were compared among 6 groups, and bending moments were calculated for comparison between un-restored and restored abutments.

RESULTS

Failure loads of un-restored abutments were affected by the abutment angle. Sixty-seven percent samples in TZ30Z and 83% samples in TZ - 15Z group fractured at the thinnest part of the zirconia abutment and exhibited lower failure load (p < .05). Failure loads of restored abutments were close to or exceeded the maximum bite force of anterior teeth, and no differences were found among six groups (p > .05). Except TZ15Z and TZ0T group, the bending moment increased with the crown construction, especially for TZ30Z and TZ - 15Z groups (p < .001).

CONCLUSIONS

The fracture strength of hybrid abutments restored with HTZ crown on Ti-Zr NDIs exceeded the bite forces of anterior teeth for all the groups and were not affected by the abutment angle.

CLINICAL RELEVANCE: In terms of fracture strength, Ti-Zr NDIs combined with angulated hybrid abutments and HTZ crowns can be used in the anterior region.