PEEK and fiberglass intra-radicular posts: influence of resin cement and mechanical cycling on push-out bond strength.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Monteiro Lara Christie, Pecorari Vanessa Gallego Arias, Gontijo Isabela Guerra, Marchi Giselle Maria, Lima Débora Alves Nunes Leite, Aguiar Flávio Henrique Baggio
Аннотация
OBJECTIVES: To evaluate the bond strength of four types of posts (pre-fabricated fiberglass post, fiberglass post anatomized with composite resin, milled fiberglass post, and milled polyetheretherketone (PEEK) post), and two types of resin cements (conventional and self-adhesive) by assessing immediate bond strength and post-mechanical aging at each root third.
MATERIALS AND METHODS: Bovine endodontically treated roots (16 groups, n = 8) were prepared and the posts were produced and luted; the specimens of aging groups were cycled (300,000 cycles under 50 N load at 1.2 Hz frequency); six slices of each root were obtained; push-out test was performed by using a universal testing machine (500 N load at 1 mm/min cross speed); fracture pattern was classified into five levels. The statistical analyses used were three-way ANOVA, Tukey's test (for bond strength), and Fisher's test (for fracture pattern) (α < 0.05).
RESULTS: Differences were found between the cements for posts (conventional: p < 0.001; self-adhesive: p = 0.002), whereas no difference was found for root region (p = 0.941; p = 0.056, respectively); analysis of each root showed significant differences for cements (p < 0.001), posts (p < 0.001), and mechanical cycling (p = 0.001); in terms of double interaction, differences were found for posts and mechanical cycling (p = 0.005); no other interactions were observed (double or triple); the fracture pattern showed difference between the groups for both cements.
CONCLUSIONS: Milled PEEK posts seem to be a good clinical option, but they require improvement of CAD-CAM technology and advances towards their adhesion.
CLINICAL RELEVANCE: Milled posts are promising and can reduce clinical time for rehabilitation of extensively destroyed teeth.
MATERIALS AND METHODS: Bovine endodontically treated roots (16 groups, n = 8) were prepared and the posts were produced and luted; the specimens of aging groups were cycled (300,000 cycles under 50 N load at 1.2 Hz frequency); six slices of each root were obtained; push-out test was performed by using a universal testing machine (500 N load at 1 mm/min cross speed); fracture pattern was classified into five levels. The statistical analyses used were three-way ANOVA, Tukey's test (for bond strength), and Fisher's test (for fracture pattern) (α < 0.05).
RESULTS: Differences were found between the cements for posts (conventional: p < 0.001; self-adhesive: p = 0.002), whereas no difference was found for root region (p = 0.941; p = 0.056, respectively); analysis of each root showed significant differences for cements (p < 0.001), posts (p < 0.001), and mechanical cycling (p = 0.001); in terms of double interaction, differences were found for posts and mechanical cycling (p = 0.005); no other interactions were observed (double or triple); the fracture pattern showed difference between the groups for both cements.
CONCLUSIONS: Milled PEEK posts seem to be a good clinical option, but they require improvement of CAD-CAM technology and advances towards their adhesion.
CLINICAL RELEVANCE: Milled posts are promising and can reduce clinical time for rehabilitation of extensively destroyed teeth.