Strain Hardening of Polypropylene Microfiber Reinforced Composite Based on Alkali-Activated Slag Matrix.

A comparative study of the fracture features, strength and deformation properties of pseudo strain-hardening composites based on alkali-activated slag and Portland cement matrices with polypropylene microfiber was carried out. Correlations between their compositions and characteristics of stress-strain diagrams under tension in bending with an additional determination of acoustic emission parameters were determined. An average strength alkali-activated slag matrix with compressive strength of 40 MPa and a high-strength Portland cement matrix with compressive strength of 70 MPa were used. The matrix compositions were selected for high filling the composites with polypropylene microfiber in the amount of 5%-vol. and 3.5%-vol. ensuring the workability at the low water-to-binder ratios of 0.22 and 0.3 for Portland cement and alkali-activated slag matrices, respectively. Deformation diagrams were obtained for all studied compositions. Peaks in the number of acoustic signals in alkali-activated slag composites were observed only in the strain-softening zone. Graphs of dependence of the rate of acoustic events occurrence in samples from the start of the test experimentally prove that this method of non-destructive testing can be used to monitor structures based on strain-hardening composites.