Influence of surface treatments and cyclic fatigue on subsurface defects and mechanical properties of zirconia frameworks.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Elraggal Alaaeldin, Silikas Nikolaos, Aboushelib Moustafa
Аннотация
OBJECTIVES: To evaluate the effect of laser fused and air abraded fluorapatite particles on flexural strength σf and fracture toughness (KIC) of Yttria tetragonal zirconia polycrystal (Y-TZP).
METHODS: 160 polished Y-TZP bars received one of the following surface treatments: airborne particle abrasion (APA) with fluorapatite glass-ceramics (FGC), APA with tribochemical silica-coated alumina (CoJet), laser fused FGC using Nd:YAG Laser (FGC + Laser), while as-sintered polished specimens served as control. Initial flexural strength σfI was measured to half of the specimens, while the rest underwent cyclic fatigue (1,000,000 cycle of 15N load and 3 s contact time) followed by measuring residual flexural strength σfR. Fractographic analysis was performed and KIC was calculated. The effect of surface treatment and fatigue on flexural strength was statistically analysed using 2-way ANOVA (α = 0.05). Weibull probability was measured to assess the reliability of flexural strength.
RESULTS: The highest σf before or after the fatigue was reported for the control group while the lowest was for FGC + Laser group. Cyclic fatigue significantly decreased the flexural strength of all groups except for FGC + Laser group. There was no significant difference between the KIC between the control and FGC groups, however, a significant reduction of KIC was found in the CoJet group, while FGC + Laser reported the significant lowest value compared to all groups (P = 0.00).
SIGNIFICANCE: Fluorapatite glass-ceramic powder offers a promising alternative for particle abrasion of zirconia-based frameworks.
METHODS: 160 polished Y-TZP bars received one of the following surface treatments: airborne particle abrasion (APA) with fluorapatite glass-ceramics (FGC), APA with tribochemical silica-coated alumina (CoJet), laser fused FGC using Nd:YAG Laser (FGC + Laser), while as-sintered polished specimens served as control. Initial flexural strength σfI was measured to half of the specimens, while the rest underwent cyclic fatigue (1,000,000 cycle of 15N load and 3 s contact time) followed by measuring residual flexural strength σfR. Fractographic analysis was performed and KIC was calculated. The effect of surface treatment and fatigue on flexural strength was statistically analysed using 2-way ANOVA (α = 0.05). Weibull probability was measured to assess the reliability of flexural strength.
RESULTS: The highest σf before or after the fatigue was reported for the control group while the lowest was for FGC + Laser group. Cyclic fatigue significantly decreased the flexural strength of all groups except for FGC + Laser group. There was no significant difference between the KIC between the control and FGC groups, however, a significant reduction of KIC was found in the CoJet group, while FGC + Laser reported the significant lowest value compared to all groups (P = 0.00).
SIGNIFICANCE: Fluorapatite glass-ceramic powder offers a promising alternative for particle abrasion of zirconia-based frameworks.