Impact of High-Speed Sintering of Three-Unit 3Y-TZP and 4Y-TZP Fixed Dental Prostheses on Fracture Load With and Without Artificial Aging.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Mayinger Felicitas, Pfefferle Regina, Reichert Axel, Stawarczyk Bogna
Аннотация
PURPOSE: To investigate the impact of high-speed sintering and artificial aging on the fracture load of three-unit zirconia fixed dental prostheses (FDPs).
MATERIALS AND METHODS: Three-unit FDPs manufactured from 3Y-TZP (Ceramill Zolid, Amann Girrbach) and 4Y-TZP (Ceramill Zolid HT+, Amann Girrbach; N = 128, n = 64/group) were sintered at 1,580°C (high-speed sintering) or at 1,450°C (control group; n = 32/subgroup). Specimens were bonded to steel abutment models using Multilink Automix (Ivoclar Vivadent), and fracture load was examined without (n = 16/subgroup) and with artificial aging (6,000 thermocycles [5°C/55°C] and 1,200,000 chewing cycles [50 N]; n = 16/subgroup). Univariate analysis of variance, unpaired t test, and Weibull modulus were computed (P < .05).
RESULTS: Sintering protocol (P = .944), artificial aging (P = .630), and zirconia material (P = .445) did not show an influence on the fracture load of three-unit FDPs. High-speed sintering led to superior Weibull modulus results for artificially aged 4Y-TZP specimens, while all other groups showed values in the same range.
CONCLUSION: The present study shows promising results for the novel high-speed sintering protocol, as it led to comparable fracture load and similar, or even superior, Weibull modulus results compared to the control group. The 4Y-TZP material presented fracture load results similar to the tried-and-tested 3Y-TZP. Artificial aging did not influence zirconia's resistance to fracture for either 3Y-TZP or 4Y-TZP.
MATERIALS AND METHODS: Three-unit FDPs manufactured from 3Y-TZP (Ceramill Zolid, Amann Girrbach) and 4Y-TZP (Ceramill Zolid HT+, Amann Girrbach; N = 128, n = 64/group) were sintered at 1,580°C (high-speed sintering) or at 1,450°C (control group; n = 32/subgroup). Specimens were bonded to steel abutment models using Multilink Automix (Ivoclar Vivadent), and fracture load was examined without (n = 16/subgroup) and with artificial aging (6,000 thermocycles [5°C/55°C] and 1,200,000 chewing cycles [50 N]; n = 16/subgroup). Univariate analysis of variance, unpaired t test, and Weibull modulus were computed (P < .05).
RESULTS: Sintering protocol (P = .944), artificial aging (P = .630), and zirconia material (P = .445) did not show an influence on the fracture load of three-unit FDPs. High-speed sintering led to superior Weibull modulus results for artificially aged 4Y-TZP specimens, while all other groups showed values in the same range.
CONCLUSION: The present study shows promising results for the novel high-speed sintering protocol, as it led to comparable fracture load and similar, or even superior, Weibull modulus results compared to the control group. The 4Y-TZP material presented fracture load results similar to the tried-and-tested 3Y-TZP. Artificial aging did not influence zirconia's resistance to fracture for either 3Y-TZP or 4Y-TZP.