American journal of dentistry · 2020
Influence of different post-endodontic restorations on the fatigue survival and biomechanical behavior of central incisors.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
De Andrade Guilherme S, Tribst João Paulo M, Orozco Esteban If, Augusto Marina G, Bottino Marco A, Borges Alexandre Ls, Anami Lilian C, Saavedra Guilherme deSFA
Аннотация
PURPOSE: To evaluate the influence of different post-endodontic techniques on the fatigue survival and biomechanical behavior of crowned restored central incisors.
METHODS: The crowns of 69 bovine incisors were cut, and the roots were treated endodontically and assigned randomly into three groups (n=23): resin composite buildup (BUP), glass fiber post-retained resin composite buildup (GFP), and cast post-and-core (CPC). They received full crown preparation with 2 mm ferrule, and a leucite-reinforced ceramic crown was cemented adhesively. Three specimens from each group were tested monotonically. The remaining specimens were subjected to the stepwise stress fatigue test until fracture or suspension after 1.5 x 10⁶ cycles in a chewing simulator. The load and step at which each specimen failed were analyzed by Kaplan-Meier and Mantel-Cox (log-rank test) statistics, followed by multiple pairwise comparisons, at 5% significance level. The three groups tested (BUP, GFP, and CPC) were 3D modeled (Rhinoceros 4.0) and the maximum principal stress (MPa) criteria were used to calculate the results using FEA.
RESULTS: There was no statistical difference between the treatments regarding the load or the number of cycles (Mantel-Cox log-rank test for trend, X²= 0.015, df=1, P= 0.901, X²=3.171, df=1, P= 0.995). Crown cracks were the predominant failure mode, and oblique root fractures were only observed in groups GFP and CPC. In endodontically treated incisors with a 2-mm ferrule, the post-endodontic treatment had no significant effect on fatigue survival. Non-restorable fractures only occurred in teeth restored with posts.
CLINICAL SIGNIFICANCE: Although the clinical significance of laboratory studies has some limitations, this study suggests that composite buildups without posts may be an option for restoring endodontically treated incisors with 2 mm ferrule height.
METHODS: The crowns of 69 bovine incisors were cut, and the roots were treated endodontically and assigned randomly into three groups (n=23): resin composite buildup (BUP), glass fiber post-retained resin composite buildup (GFP), and cast post-and-core (CPC). They received full crown preparation with 2 mm ferrule, and a leucite-reinforced ceramic crown was cemented adhesively. Three specimens from each group were tested monotonically. The remaining specimens were subjected to the stepwise stress fatigue test until fracture or suspension after 1.5 x 10⁶ cycles in a chewing simulator. The load and step at which each specimen failed were analyzed by Kaplan-Meier and Mantel-Cox (log-rank test) statistics, followed by multiple pairwise comparisons, at 5% significance level. The three groups tested (BUP, GFP, and CPC) were 3D modeled (Rhinoceros 4.0) and the maximum principal stress (MPa) criteria were used to calculate the results using FEA.
RESULTS: There was no statistical difference between the treatments regarding the load or the number of cycles (Mantel-Cox log-rank test for trend, X²= 0.015, df=1, P= 0.901, X²=3.171, df=1, P= 0.995). Crown cracks were the predominant failure mode, and oblique root fractures were only observed in groups GFP and CPC. In endodontically treated incisors with a 2-mm ferrule, the post-endodontic treatment had no significant effect on fatigue survival. Non-restorable fractures only occurred in teeth restored with posts.
CLINICAL SIGNIFICANCE: Although the clinical significance of laboratory studies has some limitations, this study suggests that composite buildups without posts may be an option for restoring endodontically treated incisors with 2 mm ferrule height.