Vascular Response After Stenting of the Renal Arteries in Pigs Using an Absorbable Sirolimus-Eluting Polymer Scaffold.
СтатьяСравнительное исследованиеНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Kischkel Sabine, Bünger Carsten M, Martin David P, Williams Simon F, Püschel Anja, Schareck Wolfgang, Grabow Niels
Аннотация
BACKGROUND: This study aims to assess the technical feasibility and biocompatibility of interventional application of a fully absorbable stent in renal arteries (RAs) of healthy pigs.
METHODS: Absorbable poly(L-lactide) (PLLA)/poly(4-hydroxybutyrate) scaffolds either loaded with sirolimus (SIR) coating or unloaded and permanent bare metal stents (BMSs) served as control were implanted interventionally into RAs of 16 female pigs via the left common iliac artery (8F-sheath). Peroral dual antiplatelet therapy was administered throughout the study. Stented RA segments were explanted after 4 weeks and assessed histomorphometrically.
RESULTS: The polymer scaffolds showed a decreased residual lumen area and higher stenosis after 4 weeks (unloaded PLLA-based: 6.5 ± 1.0 mm2 and 44.1 ± 7.4%; SIR-PLLA-based: 8.6 ± 0.5 mm2 and 32.7 ± 0.7%) compared to BMS (11.8 ± 4.3 mm2 and 23.0 ± 4.5%). Incorporation of SIR reduced the significantly higher inflammation of unloaded scaffolds; however, not to a level compared to BMS (unloaded PLLA-based: 1.3 ± 0.3; SIR-PLLA-based: 0.9 ± 0.3; BMS: 0.5 ± 0.1). In contrast, BMS showed a slightly elevated vascular injury score (0.8 ± 0.1) compared to the unloaded PLLA-based (0.6 ± 0.2) and the SIR-PLLA-based (0.4 ± 0.04) groups.
CONCLUSION: Absorbable scaffolds showed sufficient mechanical stability after porcine RA stenting. By incorporation of SIR, a significant reduction of the inflammatory and neointimal response to the unloaded polymer scaffolds was seen without systemic toxicity or thrombotic complications. However, the greater strut height of the polymer scaffold is a major limitation and need to be addressed in future work on the stent design.
METHODS: Absorbable poly(L-lactide) (PLLA)/poly(4-hydroxybutyrate) scaffolds either loaded with sirolimus (SIR) coating or unloaded and permanent bare metal stents (BMSs) served as control were implanted interventionally into RAs of 16 female pigs via the left common iliac artery (8F-sheath). Peroral dual antiplatelet therapy was administered throughout the study. Stented RA segments were explanted after 4 weeks and assessed histomorphometrically.
RESULTS: The polymer scaffolds showed a decreased residual lumen area and higher stenosis after 4 weeks (unloaded PLLA-based: 6.5 ± 1.0 mm2 and 44.1 ± 7.4%; SIR-PLLA-based: 8.6 ± 0.5 mm2 and 32.7 ± 0.7%) compared to BMS (11.8 ± 4.3 mm2 and 23.0 ± 4.5%). Incorporation of SIR reduced the significantly higher inflammation of unloaded scaffolds; however, not to a level compared to BMS (unloaded PLLA-based: 1.3 ± 0.3; SIR-PLLA-based: 0.9 ± 0.3; BMS: 0.5 ± 0.1). In contrast, BMS showed a slightly elevated vascular injury score (0.8 ± 0.1) compared to the unloaded PLLA-based (0.6 ± 0.2) and the SIR-PLLA-based (0.4 ± 0.04) groups.
CONCLUSION: Absorbable scaffolds showed sufficient mechanical stability after porcine RA stenting. By incorporation of SIR, a significant reduction of the inflammatory and neointimal response to the unloaded polymer scaffolds was seen without systemic toxicity or thrombotic complications. However, the greater strut height of the polymer scaffold is a major limitation and need to be addressed in future work on the stent design.