Influence of endodontic treatment, post insertion, and ceramic restoration on the fracture resistance of maxillary premolars.
Сравнительное исследованиеСтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Bitter K, Meyer-Lueckel H, Fotiadis N, Blunck U, Neumann K, Kielbassa A M, Paris S
Аннотация
AIM: To investigate the effects of endodontic treatment, post placement and ceramic restoration type on the fracture resistance of premolars.
METHODOLOGY: One hundred and twenty teeth maxillary premolars were allocated to four groups (A-D; n = 30). In group A, mesio-occlusal-distal-inlays with a buccal and palatal wall of 2 mm (MOD), in group B partial onlays with palatal cusp coverage and in group C total onlays with buccal and palatal cusp coverage were prepared. Group D served as untreated controls. Groups A-C were divided into three subgroups (n = 10): (i) teeth received solely the described preparations, (ii) teeth were root filled, (iii) teeth were root filled and quartz fibre posts were placed. Teeth were restored using Computer-assisted design/computer-assisted machining-ceramic-restorations and subjected to thermo-mechanical-loading; subsequently, the buccal cusp was loaded until fracture.
RESULTS: Group D revealed significantly higher fracture resistance [mean (standard deviation)] [738 (272) N] compared to all other groups (P < 0.05; post hoc test Dunnett). For groups A-C, fracture resistance was significantly affected by the restoration type (P = 0.043) and endodontic treatment/post placement (P = 0.039; 2-way anova). Group A [380 (146) N] showed significantly lower fracture resistance compared to group B [470 (158) N] (P = 0.048; post hoc test Tukey). Compared to non-endodontically treated teeth [487 (120) N], root filled teeth revealed significantly lower fracture resistance [389 (171) N] (P = 0.031).
CONCLUSION: The restoration of cavities with a remaining wall thickness of 2 mm using ceramic MOD-inlays is inferior with respect to the fracture resistance compared to partial onlay restorations. Root filled teeth without post placement show lower fracture resistance compared to non-endodontically treated teeth.
METHODOLOGY: One hundred and twenty teeth maxillary premolars were allocated to four groups (A-D; n = 30). In group A, mesio-occlusal-distal-inlays with a buccal and palatal wall of 2 mm (MOD), in group B partial onlays with palatal cusp coverage and in group C total onlays with buccal and palatal cusp coverage were prepared. Group D served as untreated controls. Groups A-C were divided into three subgroups (n = 10): (i) teeth received solely the described preparations, (ii) teeth were root filled, (iii) teeth were root filled and quartz fibre posts were placed. Teeth were restored using Computer-assisted design/computer-assisted machining-ceramic-restorations and subjected to thermo-mechanical-loading; subsequently, the buccal cusp was loaded until fracture.
RESULTS: Group D revealed significantly higher fracture resistance [mean (standard deviation)] [738 (272) N] compared to all other groups (P < 0.05; post hoc test Dunnett). For groups A-C, fracture resistance was significantly affected by the restoration type (P = 0.043) and endodontic treatment/post placement (P = 0.039; 2-way anova). Group A [380 (146) N] showed significantly lower fracture resistance compared to group B [470 (158) N] (P = 0.048; post hoc test Tukey). Compared to non-endodontically treated teeth [487 (120) N], root filled teeth revealed significantly lower fracture resistance [389 (171) N] (P = 0.031).
CONCLUSION: The restoration of cavities with a remaining wall thickness of 2 mm using ceramic MOD-inlays is inferior with respect to the fracture resistance compared to partial onlay restorations. Root filled teeth without post placement show lower fracture resistance compared to non-endodontically treated teeth.