Journal of orthopaedic surgery and research · 2021
Lugol's solution but not formaldehyde affects bone microstructure and bone mineral density parameters at the insertion site of the rotator cuff in rats.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Feichtinger Xaver, Heimel Patrick, Keibl Claudia, Hercher David, Schanda Jakob Emanuel, Kocijan Roland, Redl Heinz, Grillari Johannes, Fialka Christian, Mittermayr Rainer
Аннотация
BACKGROUND: This study aimed to investigate whether rodent shoulder specimens fixed in formaldehyde for histological and histomorphometric investigations and specimens stained using Lugol's solution for soft tissue visualization by micro-computed tomography (microCT) are still eligible to be used for bone architecture analysis by microCT.
METHODS: In this controlled laboratory study, 11 male Sprague-Dawley rats were used. After sacrifice and exarticulation both shoulders of healthy rats were assigned into three groups: (A) control group (n = 2); (B) formaldehyde group (n = 4); (C) Lugol group (n = 5). Half of the specimens of groups B and C were placed in a 4% buffered formaldehyde or Lugol's solution for 24 h, whereas the contralateral sides and all specimens of group A were stored without any additives. MicroCT of both sides performed in all specimens focused on bone mineral density (BMD) and bone microstructure parameters.
RESULTS: BMD measurements revealed higher values in specimens after placement in Lugol's solution (p < 0.05). Bone microstructure analyses showed increased BV/TV and Tb.Th values in group C (p < 0.05). Specimens of group C resulted in clearly decreased Tb.Sp values (p < 0.05) in comparison to the control group. Formaldehyde fixation showed minimally altered BMD and bone microstructure measurements without reaching any significance.
CONCLUSIONS: MicroCT scans of bone structures are recommended to be conducted natively and immediately after euthanizing rats. MicroCT scans of formaldehyde-fixed specimens must be performed with caution due to a possible slight shift of absolute values of BMD and bone microstructure. Bone analysis of specimens stained by Lugol's solution cannot be recommended.
METHODS: In this controlled laboratory study, 11 male Sprague-Dawley rats were used. After sacrifice and exarticulation both shoulders of healthy rats were assigned into three groups: (A) control group (n = 2); (B) formaldehyde group (n = 4); (C) Lugol group (n = 5). Half of the specimens of groups B and C were placed in a 4% buffered formaldehyde or Lugol's solution for 24 h, whereas the contralateral sides and all specimens of group A were stored without any additives. MicroCT of both sides performed in all specimens focused on bone mineral density (BMD) and bone microstructure parameters.
RESULTS: BMD measurements revealed higher values in specimens after placement in Lugol's solution (p < 0.05). Bone microstructure analyses showed increased BV/TV and Tb.Th values in group C (p < 0.05). Specimens of group C resulted in clearly decreased Tb.Sp values (p < 0.05) in comparison to the control group. Formaldehyde fixation showed minimally altered BMD and bone microstructure measurements without reaching any significance.
CONCLUSIONS: MicroCT scans of bone structures are recommended to be conducted natively and immediately after euthanizing rats. MicroCT scans of formaldehyde-fixed specimens must be performed with caution due to a possible slight shift of absolute values of BMD and bone microstructure. Bone analysis of specimens stained by Lugol's solution cannot be recommended.