Design of CoNiCrFeCu-xSc High-Entropy Alloy Fillers for Braze-Welding of WC-Co to Steel.

Efficient joining of hard metals to steels is crucial for supporting sustainable manufacturing under emissions strategies to minimize CO2. CoNiCrFeCu high-entropy alloy containing scandium (Sc) was designed as a filler for laser braze-welding of WC-Co and steel. The designed compositions with different Sc levels were melted and cast in a high-vacuum non-consumable arc furnace. The results showed that the as-cast microstructure was a complex mixture of a networked Ni2Si, elongated Cr-Fe-Co solid-solution phase, and Fe-Ni-Co-Cu solid-solution phase. Scandium was shown to have formed compounds with nickel/cobalt and copper. The TG-DSC analysis confirmed that the melting points of the designed compositions were between 973.7 °C and 981.5 °C. The maximum spreading area of the CoNiCrFeCu-0.9Sc composition on AISI 1045 steel was 64.83 mm2, and on the WC-Co cermet it was 78.63 mm2. The interface between the fusion zone and AISI 1045 steel exhibited an epitaxial growth of dendrites from the steel base metal. The interface between WC-Co and the fusion zone exhibited a partial penetration of brazing filler into the Co matrix, forming a metallurgical bonding between the dissimilar materials. Sc, as an alloying element in the filler metal, enhanced the bond formation because it decreased the solidus temperature and increased wetting.