Evaluation of pristine and Eu ₂O₃-added MgB ₂ ceramics for medical applications: hardness, corrosion resistance, cytotoxicity and antibacterial activity.

Nano- or micropowders of Eu2O3 were added to MgB2, resulting in a composition of (MgB2)0.975(EuO1.5)0.025. Pristine and doped samples were prepared using spark plasma sintering and tested for (i) Vickers hardness, (ii) pH evolution in phosphate-buffered saline solution, (iii) corrosion resistance (Tafel polarization curves), (iv) cytotoxicity (in vitro tests), and (v) antibacterial activity. Eu2O3 addition influenced the investigated properties. Solutions of MgB2-based samples show a relatively high saturation pH of 8.5. This value is lower than that of solutions incubated with Mg or other Mg-based biodegradable alloys reported in the literature. MgB2-based samples have lower electro-corrosion rates than Mg. Their Vickers hardness is 6.8-10.2GPa, and these values are higher than those of biodegradable Mg-based alloys. MgB2 has low in vitro biocompatibility, good antibacterial activity against Escherichia coli, and mild activity against Staphylococcus aureus. Our results suggest that MgB2-based materials deserve attention in biomedical applications, such as implants or sterile medical instruments.