New adhesive protocol improves shear bond strength of Polyetherketoneketone (PEKK).
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Arvai Robert, Baroudi Kusai, Duarte Laís, Diamantino Pedro Santos, Gimenez Mariana Gadelho, Phillippi Analucia Gebler, Saavedra Guilherme de Siqueira Ferreira Anzaloni, Waghon Zuila Maria Lobato, Gonçalves Thais Marques Simek Vega
Аннотация
OBJECTIVE: Inert surface of Polyetherketoneketone (PEKK) jeopardizes resin bonding. This study aimed to present a new adhesive protocol to improve PEKK bonding.
METHODS: A total of 360 PEKK blocks were milled, polished (maximum roughness of 0.20 µm), and randomly assigned to groups. The new protocol was applied (n = 36) and compared to conventional treatments (no treatment; sandblasting (110-µm Al2O3 and silica); no adhesive; Visiolink (Bredent); and PEKKbond (AnaxDent)) (n = 36). For the new protocol, the surface was blasted (110 µm Al2O3 and 96% isopropyl alcohol at 60 psi), followed by 96% isopropyl alcohol washing, and air drying. PEKKbond was applied (dried for 3 min at 77 °C), followed by Visiolink (dried for 3 min at 60 °C); both light-cured for 3 min (800 mW/cm2). Preopaque (GC Europe) and Opaque (AnaxDent) were applied and light-cured (5 min). Morphological topography was analyzed, and flowable gingiva-colored composite (AnaxGum, AnaxDent) was bonded. All specimens were aged for 24 h and thermocycled (5000 cycles, 5-55 °C). Shear bond strength (SBS) was measured (MPa) and data were analyzed by two-way ANOVA, Tukey, and Weibull moduli estimation (α = 0.05).
RESULTS: The highest SBS values were found in the new protocol (p < 0.05), regardless of aging. Thermocycling reduced SBS (p < 0.05), while Al2O3 and PEKKbond produced higher SBS values than silica and Visiolink, respectively (p < 0.05).
SIGNIFICANCE: The new protocol strongly improves PEKK adhesiveness, and this can reflect in the longevity of prostheses.
METHODS: A total of 360 PEKK blocks were milled, polished (maximum roughness of 0.20 µm), and randomly assigned to groups. The new protocol was applied (n = 36) and compared to conventional treatments (no treatment; sandblasting (110-µm Al2O3 and silica); no adhesive; Visiolink (Bredent); and PEKKbond (AnaxDent)) (n = 36). For the new protocol, the surface was blasted (110 µm Al2O3 and 96% isopropyl alcohol at 60 psi), followed by 96% isopropyl alcohol washing, and air drying. PEKKbond was applied (dried for 3 min at 77 °C), followed by Visiolink (dried for 3 min at 60 °C); both light-cured for 3 min (800 mW/cm2). Preopaque (GC Europe) and Opaque (AnaxDent) were applied and light-cured (5 min). Morphological topography was analyzed, and flowable gingiva-colored composite (AnaxGum, AnaxDent) was bonded. All specimens were aged for 24 h and thermocycled (5000 cycles, 5-55 °C). Shear bond strength (SBS) was measured (MPa) and data were analyzed by two-way ANOVA, Tukey, and Weibull moduli estimation (α = 0.05).
RESULTS: The highest SBS values were found in the new protocol (p < 0.05), regardless of aging. Thermocycling reduced SBS (p < 0.05), while Al2O3 and PEKKbond produced higher SBS values than silica and Visiolink, respectively (p < 0.05).
SIGNIFICANCE: The new protocol strongly improves PEKK adhesiveness, and this can reflect in the longevity of prostheses.