The hemolytic and cytotoxic properties of a zeolite-containing root filling material in vitro.

OBJECTIVE

This in vitro study characterized the hemolysis and cytotoxicity of ZUT, an experimental glass ionomer cement (GIC) sealer with an added antimicrobial-containing zeolite (0.2% Zeomic w/w).

STUDY

DESIGN

ZUT, Ketac-Cem (GIC component of ZUT), Ketac-Endo, and two AH 26 sealer formulations were tested at various times after mixing. Hemolysis produced by standardized specimens was determined spectrophotometrically (n = 6/material). Cytotoxicity was assessed by using a Millipore Filter test with a HeLa cell monolayer (n = 10/material). Tests were repeated, and results were analyzed with a one-way analysis of variance (alpha = .05).

RESULTS

Disks of AH 26 containing silver produced the most hemolysis of all test groups (P < .0001). Compared to controls, GICs and AH 26 formulations were noncytotoxic at 1 and 6 hours after mixing, respectively (P > .05). Addition of Zeomic did not increase the cytotoxic and hemolytic activity of Ketac-Cem (P > .05).

CONCLUSION

Overall results suggest ZUT is less cytotoxic than AH 26 and possesses characteristics similar to the other GIC formulations tested.