Photocatalytic and Photo-Fenton Degradation Activity of Hierarchically Structured α-Fe2O3@Fe-CeO2 and g-C3N4 Composite.

The hematite phase decorated with iron-doped cerium oxide nanoparticles (F@FC) was precipitated from cerium and iron oxalate intermediate products. The photocatalytic composite of graphitic carbon nitride (gCN) and F@FC was prepared by a simple method involving mixing the two components, followed by thermal treatment at 400 °C. According to electron microscopy, F@FC is composed of a submicron iron oxide (hematite) phase decorated with iron-doped cerium oxide nanoparticles deposited on gCN substrate. A hierarchically structured composite was observed instead of a simple mechanical mixture of α-Fe2O3, Fe-CeO2, and gCN. To observe two types of degradation activity, photocatalytic and Photo-Fenton degradation activity, Rhodamine B (RhB) was applied as the model water pollutant. The influence of the amount of photocatalyst, the RhB concentration, the presence of cations and anions, the pH, and the effect of e-, h+, •OH, and •O2- scavenging reactants were studied. The Photo-Fenton degradation exhibited high efficiency across the entire tested pH range, whereas photocatalytic degradation showed comparable activity only at acidic pH. The F@FC-gCN composite catalyst exhibited a high degree of recyclability. The degradation pathways of photocatalytic and Photo-Fenton reactions were suggested by HPLC-MS analysis of the reaction products. A notable finding of this study was the observation that the green-yellow, fluorescent intermediate Rhodamine 110 was formed during the photocatalytic degradation of RhB. However, the high reactivity of the generated •OH radicals during Photo-Fenton degradation has been demonstrated to inhibit the formation of intermediate Rhodamine 110.