Effects of tetrabutylammonium dihydrogen trifluoride etchant on bond strengths of resin composites with Ti-6Al-4V and Co-Cr alloys.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Kamada Kohji, Taira Yohsuke, Egoshi Takafumi, Kaida Kei
Аннотация
PURPOSE: This study aimed at evaluating the effects of surface treatments with tetrabutylammonium dihydrogen trifluoride (TDTF) on the bond strengths of indirect resin composites with titanium-aluminum-vanadium (Ti-6Al-4V) and cobalt-chromium (Co-Cr) alloys.
METHODS: Disk-shaped Ti-6Al-4V and Co-Cr alloy specimens were air-abraded with alumina, treated with an etchant (MEP) containing TDTF for 10 s (MEP10) or 30 s (MEP30), and rinsed with water. Subsequently, a primer containing 6-methacryloyloxyhexyl phosphonoacetate was applied to the surfaces, and the specimens were veneered with a light-curing indirect resin composite. Specimens without MEP were prepared as controls (no-MEP). Shear bond strengths were determined before or after 100,000 thermocycles, and the data were analyzed using the Steel-Dwass test (α = 0.05, n = 10).
RESULTS: No significant difference was found in the bond strengths between the Ti-6Al-4V and Co-Cr alloys. In each metal alloy, the MEP10 and MEP30 specimens exhibited higher bond strengths than the no-MEP controls after 100,000 thermocycles. Scanning electron microscopy observations revealed that submicron-pits and crevices were formed on both the metal alloys upon applying the MEP etchant.
CONCLUSION: Surface treatments with TDTF following air abrasion are useful for improving bonding durability while veneering resin composites on Ti-6Al-4V or Co-Cr alloy frameworks.
METHODS: Disk-shaped Ti-6Al-4V and Co-Cr alloy specimens were air-abraded with alumina, treated with an etchant (MEP) containing TDTF for 10 s (MEP10) or 30 s (MEP30), and rinsed with water. Subsequently, a primer containing 6-methacryloyloxyhexyl phosphonoacetate was applied to the surfaces, and the specimens were veneered with a light-curing indirect resin composite. Specimens without MEP were prepared as controls (no-MEP). Shear bond strengths were determined before or after 100,000 thermocycles, and the data were analyzed using the Steel-Dwass test (α = 0.05, n = 10).
RESULTS: No significant difference was found in the bond strengths between the Ti-6Al-4V and Co-Cr alloys. In each metal alloy, the MEP10 and MEP30 specimens exhibited higher bond strengths than the no-MEP controls after 100,000 thermocycles. Scanning electron microscopy observations revealed that submicron-pits and crevices were formed on both the metal alloys upon applying the MEP etchant.
CONCLUSION: Surface treatments with TDTF following air abrasion are useful for improving bonding durability while veneering resin composites on Ti-6Al-4V or Co-Cr alloy frameworks.