Efficient adsorption of Cr(VI) in acidic environment by nano-scaled schwertmannite prepared through pH regulation: characteristics, performances, and mechanism.

Acidic Cr(VI)-containing wastewater has received increasing attention in recent years. Schwertmannite is a suitable adsorbent for its acid resistance and good adsorption ability. However, it shows poor Cr(VI) adsorption performance under acidic conditions. Herein, inspired by the fast neutralization-mineralization process of acid mine drainage (AMD) triggered by alkaline rocks, a novel nano-scaled schwertmannite (Sch-2.7) with high Cr(VI) adsorption capacity was synthesized at constant pH of 2.7 via adding OH-. Compared with common schwertmannite (Sch), appropriate OH- effectively improved mineral yield (the precipitation efficiency of Fe: 96.75% vs. 29.93%), specific surface area (65.1 m2/g vs. 18.9 m2/g), surface group content, and further Cr(VI) adsorption ability of Sch-2.7. The maximum adsorption capacity was 54.17 (pH = 3), 61.59 (pH = 4), and 66.5 mg/g (pH = 5) for Sch-2.7, whereas only 20.35, 24.51, and 27.17 mg/g for Sch. On average, the former was 2.53 times higher than the latter. Temperature and coexisting ions had little influences on the sorption process of Sch-2.7. The mechanism analysis demonstrated that the Cr(VI) removal by Sch-2.7 was a more thermodynamic favorable process due to abundant reactive-active components on Sch-2.7 for adsorption reaction. This work provided new insight into performance optimization and application potential on Cr(VI) removal of schwertmannite.