Development of systems for targeting the regional lymph nodes for diagnostic imaging: in vivo behaviour of colloidal PEG-coated magnetite nanospheres in the rat following interstitial administration.
СтатьяПоддержка исследования: вне правительства СШАНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Illum L, Church A E, Butterworth M D, Arien A, Whetstone J, Davis S S
Аннотация
PURPOSE: Nanoparticles can be utilised for targeting drugs to the regional lymph nodes or as diagnostic agents. The surface modification of magnetite nanospheres with poly(ethylene glycol) (PEG) has been assessed by in vitro characterisation and in vivo studies following subcutaneous administration to the rat.
METHODS: Magnetite nanospheres were prepared with a grafted PEG layer using various PEG lengths from 350 to 1,000 Da. Thermogravimetric analysis was utilised to measure the adsorbed amount of PEG. Colloid stability was confirmed by measurement of the particle size and electrophoretic mobility. The kinetics of injection site drainage and lymph node retention were determined 2 hours after subcutaneous administration, for nanospheres coated with PEG lengths of 350, 550. 750, and 1,000 Da. For the 750 PEG coated nanospheres, the kinetics of distribution was determined over a 48-hour time course.
RESULTS: The distribution of the nanospheres was modified and the lymph node localisation enhanced by altering the surface coverage of PEG on the magnetic surface.
CONCLUSIONS: PEG-coated magnetite nanospheres with different surface characteristics can be utilised to target a diagnostic agent to regional lymph nodes.
METHODS: Magnetite nanospheres were prepared with a grafted PEG layer using various PEG lengths from 350 to 1,000 Da. Thermogravimetric analysis was utilised to measure the adsorbed amount of PEG. Colloid stability was confirmed by measurement of the particle size and electrophoretic mobility. The kinetics of injection site drainage and lymph node retention were determined 2 hours after subcutaneous administration, for nanospheres coated with PEG lengths of 350, 550. 750, and 1,000 Da. For the 750 PEG coated nanospheres, the kinetics of distribution was determined over a 48-hour time course.
RESULTS: The distribution of the nanospheres was modified and the lymph node localisation enhanced by altering the surface coverage of PEG on the magnetic surface.
CONCLUSIONS: PEG-coated magnetite nanospheres with different surface characteristics can be utilised to target a diagnostic agent to regional lymph nodes.