Enhanced Bone Regeneration in Variable-Type Biphasic Ceramic Phosphate Scaffolds Using rhBMP-2.

Our aim was to investigate the bone regeneration capacity of powder-type biphasic ceramic scaffold (BCP powder), block-type BCP (BCP block), and collagen-added block-type BCP (BCP collagen) with different concentrations of recombinant human bone morphogenetic protein 2 (rhBMP-2) in an animal model. Four rabbits were assigned to each of the following groups: no graft + rhBMP-2 (0.1/0.2 mg/mL), BCP powder + rhBMP-2 (0.1/0.2 mg/mL), BCP block + rhBMP-2 (0.1/0.2 mg/mL), and BCP collagen + rhBMP-2 (0.1/0.2 mg/mL), i.e., a total of 32 rabbits. Polycarbonate tubes (Φ 7 mm × 5 mm) for supporting scaffolds were fixed into a 7 mm round border. Subsequently, 0.1 mL of rhBMP-2 solutions with different concentrations was injected into the tubes. Both radiological and histomorphometric analyses showed that osteogenesis was not enhanced by increasing the concentration of rhBMP-2 in all groups at both 3 and 6 weeks. Radiological analysis showed that bone formation was higher in the BCP collagen group than in the BCP powder and BCP block groups at both rhBMP-2 concentrations at 3 weeks. rhBMP-2 enhanced bone formation; however, as the concentration increased, bone formation could not be enhanced infinitely. Collagen-added alloplastic graft material may be useful for mediating rapid bone formation in initial stages.