Chloroprene and Butadiene Rubber (CR/BR) Blends Cross-Linked with Metal Oxides: INFLUENCE of Vulcanization Temperature on Their Rheological, Mechanical, and Thermal Properties.

This paper aimed to evaluate the effect of cross-linking temperature on the rheological, mechanical, and thermal properties of CR/BR compositions cross-linked with zinc oxide, iron(III) oxide, or copper(II) oxide. Properties of CR/BR compounds were studied at four temperatures: 140, 160, 180, and 200 °C. The lowest activation energy of vulcanization was shown by blends cross-linked with ZnO, and the highest activation energy of vulcanization was shown by samples with Fe2O3. Blends cured with ZnO or Fe2O3 showed higher cross-linking activity than CuO. Higher temperatures enhanced the degree of cross-linking in the CR/BR composite cured with ZnO or CuO but slightly reduced it for the CR/BR/Fe2O3 vulcanizates. The highest tensile strength was observed for the CR/BR/Fe2O3 product. However, compositions cured with ZnO exhibited the best aging resistance. The CR/BR compounds cured with ZnO at high temperatures had the highest tear strength (16.8 N/mm), while samples containing CuO as a curing agent showed declining tear strength with temperature. DSC confirmed a single glass transition (~36 °C), indicating good elastomers dispersion. Infrared and SEM analyses confirmed effective cross-linking and blend compatibility.