Tail state mediated conduction in zinc tin oxide thinfilm phototransistors under below bandgap optical excitation.

We report on the appearance of a strong persistent photoconductivity (PPC) and conductor-like behaviour in zinc tin oxide (ZTO) thinfilm phototransistors. The active ZTO channel layer was prepared by remote plasma reactive sputtering and possesses an amorphous structure. Under sub-bandgap excitation of ZTO with UV light, the photocurrent reaches as high as ~ 10-4 A (a photo-to-dark current ratio of ~ 107) and remains close to this high value after switching off the light. During this time, the ZTO TFT exhibits strong PPC with long-lasting recovery time, which leads the appearance of the conductor-like behaviour in ZTO semiconductor. In the present case, the conductivity changes over six orders of magnitude, from ~ 10-7 to 0.92/Ω/cm. After UV exposure, the ZTO compound can potentially remain in the conducting state for up to a month. The underlying physics of the observed PPC effect is investigated by studying defects (deep states and tail states) by employing a discharge current analysis (DCA) technique. Findings from the DCA study reveal direct evidence for the involvement of sub-bandgap tail states of the ZTO in the strong PPC, while deep states contribute to mild PPC.