Gorler Oguzhan, Dogan Derya Ozdemir, Ulgey Melih, Goze Aysegul, Hubbezoğlu Ihsan, Zan Recai, Ozdemir Ali Kemal
Аннотация
OBJECTIVE: The present study was to assess the effect of surface treatments of Er:YAG, Nd:YAG, and Ho:YAG lasers on the tensile bond strength of a silicone-based resilient liner to an acrylic denture in an in vitro setting.
METHODS: Experimental dumbbell-shaped specimens (75 mm) were produced by combining two acrylate pieces fabricated from heat-polymerized acrylic resin (36 mm) with 3 mm of Molloplast(®)-B filling between them. The specimens (n=200) were randomly divided in half for thermocycling, and each 100 specimen set was randomized into five groups (n=20) with different surface treatments: control (no surface treatment), sandblasting, Er:YAG laser, Nd:YAG laser, and Ho:YAG laser. A tensile bond strength test was performed. The effect of the laser surface treatments was examined with scanning electron microscopy.
RESULTS: Only the Er:YAG laser increased the tensile bond strength compared with the other treatments. The other laser groups showed lower bond strengths. The Ho:YAG laser resulted in considerably reduced tensile bond strength. The scanning electron microscopy images showed that applying laser surface treatments modified the surface of the denture base resin.
CONCLUSIONS: There was not an overall improvement with the use of the studied laser modalities in the adhesion quality of resilient denture liner to acrylic resin, although Er:YAG laser showed a potential to improve their adhesion. These laser modalities need to be subjected to further studies to determine optimal setup for use in prosthodontics.
METHODS: Experimental dumbbell-shaped specimens (75 mm) were produced by combining two acrylate pieces fabricated from heat-polymerized acrylic resin (36 mm) with 3 mm of Molloplast(®)-B filling between them. The specimens (n=200) were randomly divided in half for thermocycling, and each 100 specimen set was randomized into five groups (n=20) with different surface treatments: control (no surface treatment), sandblasting, Er:YAG laser, Nd:YAG laser, and Ho:YAG laser. A tensile bond strength test was performed. The effect of the laser surface treatments was examined with scanning electron microscopy.
RESULTS: Only the Er:YAG laser increased the tensile bond strength compared with the other treatments. The other laser groups showed lower bond strengths. The Ho:YAG laser resulted in considerably reduced tensile bond strength. The scanning electron microscopy images showed that applying laser surface treatments modified the surface of the denture base resin.
CONCLUSIONS: There was not an overall improvement with the use of the studied laser modalities in the adhesion quality of resilient denture liner to acrylic resin, although Er:YAG laser showed a potential to improve their adhesion. These laser modalities need to be subjected to further studies to determine optimal setup for use in prosthodontics.